Catalytic pyrolysis using UZM-39 aluminosilicate zeolite

ABSTRACT

A new family of coherently grown composites of TUN and IMF zeotypes has been synthesized and shown to be effective catalysts for catalytic pyrolysis of biomass. These zeolites are represented by the empirical formula.
 
Na n M m   n+ R r Q q Al 1-x E x Si y O z  
 
where M represents zinc or a metal or metals from Group 1, Group 2, Group 3 or the lanthanide series of the periodic table, R is an A,Ω-dihalosubstituted paraffin such as 1,4-dibromobutane, Q is a neutral amine containing 5 or fewer carbon atoms such as 1-methylpyrrolidine and E is a framework element such as gallium. The process involves contacting a carbonaceous biomass feedstock with UZM-39 at pyrolysis conditions to produce pyrolysis gases comprising hydrocarbons. The catalyst catalyzes a deoxygenation reaction converting oxygenated hydrocarbons into hydrocarbons and removing the oxygen as carbon oxides and water. A portion of the pyrolysis gases is condensed to produce low oxygen biomass-derived pyrolysis oil.

CROSS REFERENCE TO RELATED APPLICATION

This application claims the benefit of priority of U.S. Provisional Application 61/736,390, filed Dec. 12, 2012, the contents of which are hereby incorporated by reference in its entirety.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

This invention was made with Government support under ZFT-O-40619-01 awarded by the United States Department of Energy. The Government has certain rights in the invention.

FIELD OF THE INVENTION

This invention relates to using a new family of aluminosilicate zeolites designated UZM-39 as the catalytic composite for catalytic pyrolysis of biomass. The zeolite family is represented by the empirical formula of: Na_(n)M_(m) ^(k+)T_(t)Al_(1-x)E_(x)Si_(y)O_(z) where M represents a metal or metals from zinc or Group 1 (IUPAC 1), Group 2 (IUPAC 2), Group 3 (IUPAC 3) or the lanthanide series of the periodic table, T is the organic directing agent derived from reactants R and Q where R is an A,Ω-dihalosubstituted alkane such as 1,4-dibromobutane and Q is at least one neutral amine having 6 or fewer carbon atoms such as 1-methylpyrrolidine. E is a framework element such as gallium.

BACKGROUND OF THE INVENTION

Zeolites are crystalline aluminosilicate compositions which are microporous and which are formed from corner sharing AlO₂ and SiO₂ tetrahedra. Numerous zeolites, both naturally occurring and synthetically prepared, are used in various industrial processes. Synthetic zeolites are prepared via hydrothermal synthesis employing suitable sources of Si, Al and structure directing agents such as alkali metals, alkaline earth metals, amines, or organoammonium cations. The structure directing agents reside in the pores of the zeolite and are largely responsible for the particular structure that is ultimately formed. These species balance the framework charge associated with aluminum and can also serve as space fillers. Zeolites are characterized by having pore openings of uniform dimensions, having a significant ion exchange capacity, and being capable of reversibly desorbing an adsorbed phase which is dispersed throughout the internal voids of the crystal without significantly displacing any atoms which make up the permanent zeolite crystal structure. Zeolites can be used as catalysts for hydrocarbon conversion reactions, which can take place on outside surfaces as well as on internal surfaces within the pore.

One particular zeolite, designated TNU-9, was first disclosed by Hong et al. in 2004, (J. Am. Chem. Soc. 2004, 126, 5817-26) and then in a Korean Patent granted in 2005, KR 480229. This report and patent was followed by a full report of the synthesis in 2007 (J. Am. Chem. Soc. 2007, 129, 10870-85). These papers describe the synthesis of TNU-9 from the flexible dicationic structure directing agent, 1,4-bis(N-methylpyrrolidinium)butane dibromide in the presence of sodium. After the structure of TNU-9 was solved (Nature, 2006, 444, 79-81), the International Zeolite Association Structure Commission gave the code of TUN to this zeolite structure type, see Atlas of Zeolite Framework Types, which is maintained by the International Zeolite Association Structure Commission at http://www.iza-structure.org/databases/. The TUN structure type was found to contain 3 mutually orthogonal sets of channels in which each channel is defined by a 10-membered ring of tetrahedrally coordinated atoms. In addition, 2 different sizes of 10-membered ring channels exist in the structure.

Another particular zeolite, IM-5 was first disclosed by Benazzi, et al. in 1996 (FR96/12873; WO98/17581) who describe the synthesis of IM-5 from the flexible dicationic structure directing agent, 1,5-bis(N-methylpyrrolidinium)pentane dibromide or 1,6-bis(N-methylpyrrolidinium)hexane dibromide in the presence of sodium. After the structure of IM-5 was solved by Baerlocher et al. (Science, 2007, 315, 113-6), the International Zeolite Structure Commission gave the code of IMF to this zeolite structure type, see Atlas of Zeolite Framework Types. The IMF structure type was also found to contain three mutually orthogonal sets of channels in which each channel is defined by a 10-membered ring of tetrahedrally coordinated atoms, however, connectivity in the third dimension is interrupted every 2.5 nm, therefore diffusion is somewhat limited. In addition, multiple different sizes of 10-membered ring channels exist in the structure.

Applicants have successfully prepared a new family of materials designated UZM-39. The topology of the materials is similar to that observed for TNU-9 and IM-5. The materials are prepared via the use of a mixture of simple commercially available structure directing agents, such as 1,4-dibromobutane and 1-methylpyrrolidine, in concert with Na⁺ using the Layered Material Conversion approach to zeolite synthesis (described below). This type of zeolite may be used as a catalyst in pyrolyzing a carbonaceous biomass feedstock to produce pyrolysis gases comprising hydrocarbons. The catalyst catalyzes a deoxygenation reaction converting at least a portion of the oxygenated hydrocarbons into hydrocarbons and removing the oxygen as carbon oxides and water. A condensable portion of the pyrolysis gases is condensed to low oxygen biomass-derived pyrolysis oil.

SUMMARY OF THE INVENTION

As stated, the present invention relates to using a new catalytic composite comprising coherently grown composite of TUN and IMF zeotypes designated UZM-39 as at the catalytic composite in a process for pyrolyzing a carbonaceous biomass feedstock. The microporous crystalline zeolite has a three-dimensional framework of at least AlO₂ and SiO₂ tetrahedral units and an empirical composition in the as synthesized and anhydrous basis expressed by an empirical formula of: Na_(n)M_(m) ^(k+)T_(t)Al_(1-x)E_(x)Si_(y)O_(z) where “n” is the mole ratio of Na to (Al+E) and has a value from approximately 0.05 to 0.5, M represents at least one metal selected from the group consisting of zinc, Group 1 (IUPAC 1), Group 2 (IUPAC 2), Group 3 (IUPAC 3), and the lanthanide series of the periodic table, and any combination thereof, “m” is the mole ratio of M to (Al+E) and has a value from 0 to 0.5, “k” is the average charge of the metal or metals M, T is the organic structure directing agent or agents derived from reactants R and Q where R is an A,Ω-dihalogen substituted alkane having from 3 to 6 carbon atoms and Q is at least one neutral monoamine having 6 or fewer carbon atoms, “t” is the mole ratio of N from the organic structure directing agent or agents to (Al+E) and has a value of from about 0.5 to about 1.5, E is an element selected from the group consisting of gallium, iron, boron and combinations thereof, “x” is the mole fraction of E and has a value from 0 to about 1.0, “y” is the mole ratio of Si to (Al+E) and varies from greater than 9 to about 25 and “z” is the mole ratio of O to (Al+E) and has a value determined by the equation: z=(n+k·m+3+4·y)/2 and is characterized in that it has TUN regions and IMF regions that are coherently aligned so that the [010]_(TUN) zone axis and the [001]_(IMF) zone axis are parallel to each other and there is continuity of crystal planes of type (002)_(TUN) and (060)_(IMF), where the indexing is referred to monoclinic C_(2/m) and orthorhombic C_(mem) unit cells for TUN and IMF respectively.

The microporous crystalline zeolite may also be described as having a three-dimensional framework of at least AlO₂ and SiO₂ tetrahedral units and an empirical composition in the as synthesized and anhydrous basis expressed by an empirical formula of: Na_(n)M_(m) ^(k+)T_(t)Al_(1-x)E_(x)Si_(y)O_(z) where “n” is the mole ratio of Na to (Al+E) and has a value from approximately 0.05 to 0.5, M represents a metal or metals from Group 1 (IUPAC 1), Group 2 (IUPAC 2), Group 3 (IUPAC 3), the lanthanide series of the periodic table or zinc, “m” is the mole ratio of M to (Al+E) and has a value from 0 to 0.5, “k” is the average charge of the metal or metals M, T is the organic structure directing agent or agents derived from reactants R and Q where R is an A,Ω-dihalogen substituted alkane having between 3 and 6 carbon atoms and Q is at least one neutral monoamine having 6 or fewer carbon atoms, “t” is the mole ratio of N from the organic structure directing agent or agents to (Al+E) and has a value of from 0.5 to 1.5, E is an element selected from the group consisting of gallium, iron, boron and combinations thereof, “x” is the mole fraction of E and has a value from 0 to about 1.0, “y” is the mole ratio of Si to (Al+E) and varies from greater than 9 to about 25 and “z” is the mole ratio of O to (Al+E) and has a value determined by the equation: z=(n+k·m+3+4·y)/2 and the zeolite is characterized in that it has the x-ray diffraction pattern having at least the d-spacings and intensities set forth in Table A1

TABLE A1 2θ d (Å) I/Io % 7.17-7.21 12.25-12.31 vw-m  7.5-8.1* 11.78-10.91 w-m 8.88 9.95 m 9.17 9.63 w-m 12.47-12.62 7.09-7.00 w-m 17.7 5.01 vw-m 22.8-23.2 3.90-3.83 vs 23.39-23.49 3.80-3.78 m-s 25.01-25.31 3.56-3.52 m 28.74-29.25 3.10-3.05 w-m 45.08-45.29 2.01-2.00 w *composite peak consisting of multiple overlapping reflections The zeolite is thermally stable up to a temperature of greater than 600° C. in one embodiment and at least 800° C. in another embodiment.

The Layered Material Conversion approach may be used for preparing the crystalline microporous zeolite described above. The process comprises forming a reaction mixture containing reactive sources of Na, R, Q, Al, Si, seeds of a layered material L and optionally E and/or M and heating the reaction mixture at a temperature of about 150° C. to about 200° C., about 155° C. to about 190° C., or about 160° C. to about 180° C., for a time sufficient to form the zeolite. L does not have the same zeotype as the UZM-39 coherently grown composite. The reaction mixture has a composition expressed in terms of mole ratios of the oxides of: a-bNa₂O:bM_(n/2)O:cRO:dQ:1-eAl₂O₃ :eE₂O₃ :fSiO₂ :gH₂O where “a” has a value of about 10 to about 30, “b” has a value of 0 to about 30, “c” has a value of about 1 to about 10, “d” has a value of about 2 to about 30, “e” has a value of 0 to about 1.0, “f” has a value of about 30 to about 100, “g” has a value of about 100 to about 4000. Additionally, the reaction mixture comprises from about 1 to about 10 wt.-% of seed zeolite L based on the amount of SiO₂ in the reaction mixture, e.g., if there is 100 g of SiO₂ in the reaction mixture, from about 1 to about 10 g of seed zeolite L would be added to the reaction mixture. With this number of reactive reagent sources, many orders of addition can be envisioned. Typically, the aluminum reagent is dissolved in the sodium hydroxide prior to adding the silica reagents. As can be seen in the examples, reagents R and Q can be added together or separately in many different orders of addition.

The invention involves a process of pyrolyzing a carbonaceous biomass feedstock in the presence of a catalyst wherein the catalyst is the UZM-39 zeolite to produce pyrolysis gases comprising hydrocarbons. The catalyst catalyzes a deoxygenation reaction converting at least a portion of the oxygenated hydrocarbons into hydrocarbons and removing the oxygen as carbon oxides and water. A condensable portion of the pyrolysis gases is condensed to low oxygen biomass-derived pyrolysis oil.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is an XRD pattern of the UZM-39 zeolite formed in Example 1. This pattern shows the UZM-39 zeolite in the as-synthesized form.

FIG. 2 is also an XRD pattern of the UZM-39 zeolite formed in Example 1. This pattern shows the UZM-39 zeolite after calcination.

FIG. 3 is an XRD pattern of the UZM-39 zeolite formed in Example 16. This pattern shows the UZM-39 zeolite in the as-synthesized form.

FIG. 4 is also an XRD pattern of the UZM-39 zeolite formed in Example 16. This pattern shows the UZM-39 zeolite in the H⁺ form.

FIG. 5 is an XRD pattern of the UZM-39 zeolite formed in Example 28. This pattern shows the UZM-39 zeolite in the as-synthesized form.

FIG. 6 is also an XRD pattern of the UZM-39 zeolite formed in Example 28. This pattern shows the UZM-39 zeolite in the H⁺ form.

FIG. 7 shows the results of high-resolution scanning electron microscopy characterization of the UZM-39 product of Example 1. The electron micrograph shows that UZM-39 forms in lathes which assemble into rectangular rod particles, often with a starburst cluster arrangement. The starburst cluster rods of UZM-39 can be seen in the scanning electron microscopy results of FIG. 7.

FIG. 8 shows the results of high-resolution scanning electron microscopy characterization of a different UZM-39, that of the product of Example 18. The electron micrograph also shows lathes assembled into rectangular rod particles with a number of starburst cluster arrangements.

FIG. 9 shows a wireframe representation of the TUN framework in the AC plane (left). Each vertex is a T-site and in the middle of each stick is an oxygen atom. A wireframe representation of the IMF framework in the AB plane is shown to the right. Along these projections, both the TUN and IMF frameworks contain nearly identical projections of chains of 5-rings connected by 6-rings and 10-ring channels.

FIG. 10 shows the results of transmission electron microscopy characterization of the UZM-39 product of Example 17 using high resolution imaging and computed optical diffractograms. The results show that UZM-39 is comprised of a coherently grown composite structure of TUN and IMF zeotypes.

FIG. 11 is an electron diffraction analysis of the cross sectioned rod particle of FIG. 10 and shows that from what appears to be a single-crystalline zeolite particle, areas that index to [010] zone axis of TUN and to [001] zone axis of IMF are found. The TUN regions and IMF regions are coherently aligned.

FIG. 12 is a plot of the low angle region in XRD analysis of materials showing that small percentages of IMF can be determined in samples largely consisting of TUN.

FIG. 13 is a plot of the low angle region in XRD analysis of materials showing that small percentages of TUN can be determined in samples largely consisting of IMF.

DETAILED DESCRIPTION OF THE INVENTION

Applicants have prepared a catalytic component suitable for catalyzing the pyrolysis of carbonaceous biomass where the catalyst is an aluminosilicate zeolite whose topological structure is related to TUN as described in Atlas of Zeolite Framework Types, which is maintained by the International Zeolite Association Structure Commission at http://www.iza-structure.org/databases/, the member of which has been designated TNU-9. As will be shown in detail, UZM-39 is different from TNU-9 in a number of its characteristics including its x-ray diffraction pattern (XRD). UZM-39 is also related to IMF as described in the Atlas of Zeolite Framework Types, the member of which has been designated IM-5. As will be shown in detail, UZM-39 is different from TNU-9 and IM-5 in a number of its characteristics including its x-ray diffraction pattern. The instant microporous crystalline zeolite (UZM-39) has an empirical composition in the as synthesized and anhydrous basis expressed by an empirical formula of: Na_(n)M_(m) ^(k+)T_(t)Al_(1-x)E_(x) Si _(y)O_(z) where “n” is the mole ratio of Na to (Al+E) and has a value from approximately 0.05 to 0.5, M represents a metal or metals selected from the group consisting of zinc, Group 1 (IUPAC 1), Group 2 (IUPAC 2), Group 3 (IUPAC 3), the lanthanide series of the periodic table, and any combination thereof, “m” is the mole ratio of M to (Al+E) and has a value from 0 to 0.5, “k” is the average charge of the metal or metals M, T is the organic structure directing agent or agents derived from reactants R and Q where R is an A,Ω-dihalogen substituted alkane having between 3 and 6 carbon atoms and Q is at least one neutral monoamine having 6 or fewer carbon atoms, “t” is the mole ratio of N from the organic structure directing agent or agents to (Al+E) and has a value of from 0.5 to 1.5, E is an element selected from the group consisting of gallium, iron, boron and combinations thereof, “x” is the mole fraction of E and has a value from 0 to about 1.0, “y” is the mole ratio of Si to (Al+E) and varies from greater than 9 to about 25 and “z” is the mole ratio of O to (Al+E) and has a value determined by the equation: z=(n+k·m+3+4·y)/2 where M is only one metal, then the weighted average valence is the valence of that one metal, i.e. +1 or +2. However, when more than one M metal is present, the total amount of: M_(m) ^(k+)=M_(m1) ^((k1)+)+M_(m2) ^((k2)+)+M_(m3) ^((k3)+)+M_(m4) ^((k4)+)+ . . . and the weighted average valence “k” is given by the equation:

$k = \frac{{m\;{1 \cdot k}\; 1} + {m\;{2 \cdot k}\; 2} + {m\;{3 \cdot k}\; 3\mspace{14mu}\ldots}}{{m\; 1} + {m\; 2} + {m\; 3\mspace{14mu}\ldots}}$

The microporous crystalline zeolite, UZM-39, may be synthesized by a hydrothermal crystallization of a reaction mixture prepared by combining reactive sources of sodium, organic structure directing agent or agents T, aluminum, silicon, seeds of a layered material L, and optionally E, M, or both. The sources of aluminum include but are not limited to aluminum alkoxides, precipitated aluminas, aluminum metal, aluminum hydroxide, sodium aluminate, aluminum salts and alumina sols. Specific examples of aluminum alkoxides include, but are not limited to aluminum sec-butoxide and aluminum ortho isopropoxide. Sources of silica include but are not limited to tetraethylorthosilicate, colloidal silica, precipitated silica and alkali silicates. Sources of sodium include but are not limited to sodium hydroxide, sodium aluminate, sodium bromide, and sodium silicate.

T is the organic structure directing agent or agents derived from reactants R and Q where R is an A,Ω-dihalogen substituted alkane having between 3 and 6 carbon atoms and Q comprises at least one neutral monoamine having 6 or fewer carbon atoms. R may be an A,Ω-dihalogen substituted alkane having between 3 and 6 carbon atoms selected from the group consisting of 1,3-dichloropropane, 1,4-dichlorobutane, 1,5-dichloropentane, 1,6-dichlorohexane, 1,3-dibromopropane, 1,4-dibromobutane, 1,5-dibromopentane, 1,6-dibromohexane, 1,3-diiodopropane, 1,4-diiodobutane, 1,5-diiodopentane, 1,6-diiodohexane and combinations thereof. Q comprises at least one neutral monoamine having 6 or fewer carbon atoms such as 1-ethylpyrrolidine, 1-methylpyrrolidine, 1-ethylazetidine, 1-methylazetidine, triethylamine, diethylmethylamine, dimethylethylamine, trimethylamine, dimethylbutylamine, dimethylpropylamine, dimethylisopropylamine, methylethylpropylamine, methylethylisopropylamine, dipropylamine, diisopropylamine, cyclopentylamine, methylcyclopentylamine, hexamethyleneimine. Q may comprise combinations of multiple neutral monoamines having 6 or fewer carbon atoms.

L comprises at least one seed of a layered zeolite. Suitable seed zeolites are layered materials that are microporous zeolites with crystal thickness in at least one dimension of less than about 30 to about 50 nm. The microporous materials have pore diameters of less than about 2 nm. The seed layered zeolite is of a different zeotype than the UZM-39 coherently grown composite being synthesized. Examples of suitable layered materials include but are not limited to UZM-4M (U.S. Pat. No. 6,776,975), UZM-5 (U.S. Pat. No. 6,613,302), UZM-8 (U.S. Pat. No. 6,756,030), UZM-8HS (U.S. Pat. No. 7,713,513), UZM-26 (US-2010-0152023-A1), UZM-27 (U.S. Pat. No. 7,575,737), BPH, FAU/EMT materials, *BEA or zeolite Beta, members of the MWW family such as MCM-22P and MCM-22, MCM-36, MCM-49, MCM-56, ITQ-1, ITQ-2, ITQ-30, ERB-1, EMM-10P and EMM-10, SSZ-25, and SSZ-70 as well as smaller microporous materials such as PREFER (pre ferrierite), NU-6 and the like.

M represents at least one exchangeable cation of a metal or metals from Group 1 (IUPAC 1), Group 2 (IUPAC 2), Group 3 (IUPAC 3), or the lanthanide series of the periodic table and or zinc. Specific examples of M include but are not limited to lithium, potassium, rubidium, cesium, magnesium, calcium, strontium, barium, zinc, yttrium, lanthanum, gadolinium, and mixtures thereof. Reactive sources of M include, but are not limited to, the group consisting of halide, nitrate, sulfate, hydroxide, or acetate salts. E is an element selected from the group consisting of gallium, iron, boron and combinations thereof, and suitable reactive sources include, but are not limited to, boric acid, gallium oxyhydroxide, gallium sulfate, gallium nitrate, ferric sulfate, ferric nitrate, ferric chloride and mixtures thereof.

The reaction mixture containing reactive sources of the desired components can be described in terms of molar ratios of the oxides by the formula: a-bNa₂O:bM_(n/2)O:cRO:dQ:1-eAl₂O₃ :eE₂O₃ :fSiO₂ :gH₂O where “a” has a value of about 10 to about 30, “b” has a value of 0 to about 30, “c” has a value of about 1 to about 10, “d” has a value of about 2 to about 30, “e” has a value of 0 to about 1.0, “f” has a value of about 30 to about 100, “g” has a value of about 100 to about 4000. Additionally in the reaction mixture is from about 1 to about 10 wt.-% of seed zeolite L based on the amount of SiO₂ in the reaction, e.g., if there is 100 g of SiO₂ in the reaction mixture, from about 1 to about 10 g of seed zeolite L would be added. The examples demonstrate a number of specific orders of addition for the reaction mixture which lead to UZM-39. However, as there are at least 6 starting materials, many orders of addition are possible. For example, the seed crystals L can be added as the last ingredient to the reaction mixture, to the reactive Si source, or at other suitable points. Also, if alkoxides are used, it is preferred to include a distillation or evaporative step to remove the alcohol hydrolysis products. While the organic structure directing agents R and Q can be added separately or together to the reaction mixture at a number of points in the process, it is preferred to mix R and Q together at room temperature and add the combined mixture to a cooled mixture of reactive Si, Al and Na sources maintained at 0-10° C. Alternatively, the mixture of R and Q, after mixing at room temperature, could be cooled and the reactive sources of Si, Al and Na added to the organic structure directing agent mixture while maintaining a temperature of 0-10° C. In an alternative embodiment, the reagents R and Q could be added, separately or together, to the reaction mixture at room temperature.

The reaction mixture is then reacted at a temperature of about 150° C. to about 200° C., about 155° C. to about 190° C., or about 160° C. to about 180° C., for a period of about 1 day to about 3 weeks and preferably for a time of about 3 days to about 12 days in a stirred, sealed reaction vessel under autogenous pressure. After crystallization is complete, the solid product is isolated from the heterogeneous mixture by means such as filtration or centrifugation, and then washed with deionized water and dried in air at ambient temperature up to about 100° C.

The as-synthesized coherently grown composite of TUN and IMF zeotypes, UZM-39, is characterized by the x-ray diffraction pattern, having at least the d-spacings and relative intensities set forth in Tables A1-A3 below. Diffraction patterns herein were obtained using a typical laboratory powder diffractometer, utilizing the K_(α), line of copper; Cu K alpha. From the position of the diffraction peaks represented by the angle 2theta, the characteristic interplanar distances d_(hkl) of the sample can be calculated using the Bragg equation. The intensity is calculated on the basis of a relative intensity scale attributing a value of 100 to the line representing the strongest peak on the X-ray diffraction pattern, and then: very weak (vw) means less than 5; weak (w) means less than 15; medium (m) means in the range 15 to 50; strong (s) means in the range 50 to 80; very strong (vs) means more than 80. Intensities may also be shown as inclusive ranges of the above. The X-ray diffraction patterns from which the data (d spacing and intensity) are obtained are characterized by a large number of reflections some of which are broad peaks or peaks which form shoulders on peaks of higher intensity. Some or all of the shoulders may not be resolved. This may be the case for samples of low crystallinity, of particular coherently grown composite structures or for samples with crystals which are small enough to cause significant broadening of the X-rays. This can also be the case when the equipment or operating conditions used to produce the diffraction pattern differ significantly from those used in the present case.

The X-ray diffraction pattern for UZM-39 contains many peaks. Examples of the x-ray diffraction patterns for various as-synthesized UZM-39 products are shown in FIGS. 1, 3, and 5. Those peaks characteristic of UZM-39 are shown in Tables A1-A3 for various coherently grown composite structures. Additional peaks, particularly those of very weak intensity, may also be present. All peaks of medium or higher intensity present in the UZM-39 family of coherently grown composite structures are represented in at least Table A3.

Table A1 contains selected d-spacings and relative intensities of the UZM-39 X-ray diffraction pattern. The relative intensities are shown as a range covering UZM-39 materials with varying relative amounts of TUN and IMF zeotypes.

TABLE A1 2θ d (Å) I/Io % 7.17-7.21 12.25-12.31 vw-m  7.5-8.1* 11.78-10.91 w-m 8.88 9.95 M 9.17 9.63 w-m 12.47-12.62 7.09-7.00 w-m 17.7 5.01 vw-m 22.8-23.2 3.90-3.83 Vs 23.39-23.49 3.80-3.78 m-s 25.01-25.31 3.56-3.52 M 28.74-29.25 3.10-3.05 w-m 45.08-45.29 2.01-2.00 W *composite peak consisting of multiple overlapping reflections

The zeolite may be further characterized by the x-ray diffraction pattern having at least the d-spacings and intensities set forth in Table A2 where the d-spacings and intensities are provided at different relative concentrations of the components of the coherently grown composite structure.

TABLE A2 I II III high TUN, low IMF med TUN, med IMF low TUN, high IMF 2-Theta d(†) I/Io % 2-Theta d(†) I/Io % 2-Theta d(†) I/Io % 7.21 12.25 w-m 7.17 12.31 w-m 7.21 12.25 vw 7.5-8.1* 11.78-10.91 w-m 7.5-8.1* 11.78-10.91 w-m 7.5-8.1* 11.78-10.91 w-m 8.88 9.95 m 8.88 9.95 s 8.88 9.95 m 9.17 9.63 m 9.16 9.65 m 9.17** 9.63 w-m 9.34** 9.46 vw-w 9.30 9.50 m 9.33 9.47 m 12.62 7.00 w 12.50 7.08 w-m 12.47 7.09 w-m 17.70 5.01 vw-w 17.72 5.00 w-m 17.70 5.01 vw-w 19.20 4.62 w-m 22.8-23.2* 3.90-3.83 vs 18.71 4.74 w-m 22.89 3.88 vs 23.43 3.79 s 22.55 3.94 m 23.49 3.78 m 25.12 3.54 m 23.03 3.86 vs 25.31 3.52 m 28.74-29.25* 3.10-3.05 w-m 23.39 3.80 s 29.10 3.07 w 45.29 2.00 w 25.01 3.56 m 45.08 2.01 w 28.76 3.10 w-m 45.08 2.01 w *composite peak consisting of multiple overlapping reflections **typically a shoulder

The zeolite may be yet further characterized by the x-ray diffraction pattern having at least the d-spacings and intensities set forth in Table A3 where the d-spacings and intensities are provided at different relative concentrations of the components of the coherently grown composite structure.

TABLE A3 I II III high TUN, low IMF med TUN, med IMF low TUN, high IMF 2-Theta d(†) I/Io % 2-Theta d(†) I/Io % 2-Theta d(†) I/Io % 7.21 12.25 w-m 7.17 12.31 w-m 7.21 12.22 vw 7.5-8.1* 11.78-10.91 w-m 7.5-8.1* 11.78-10.91 w-m 7.5-8.1* 11.78-10.91 w-m 8.88 9.95 m 8.88 9.95 m-s 8.88 9.95 m 9.17 9.63 m 9.16 9.65 m 9.17** 9.63 w-m 9.34** 9.46 vw-w 9.30 9.50 m 9.33 9.47 m 9.98 8.85 vw 12.50 7.08 w-m 12.47 7.09 w-m 11.68 7.57 vw 15.27 5.80 vw-w 12.85 6.88 vw 12.62 7.00 w 15.58 5.68 w 14.62 6.05 vw-w 13.69 6.46 vw-w 17.70 5.01 vw-w 15.27 5.80 w 15.33 5.77 vw-w 18.72 4.74 vw-m 15.57 5.68 w 16.48 5.37 vw-w 19.28 4.60 w 16.60 5.34 w 17.01 5.20 vw 22.61** 3.93 w-m 17.70 5.01 vw-w 17.70 5.01 vw-w 22.8-23.2* 3.90-3.83 vs 18.71 4.74 w-m 19.20 4.62 w-m 23.43 3.79 s 19.30 4.59 w 21.59 4.11 vw-w 24.20 3.68 m 22.55 3.94 m 22.61** 3.93 w-m 25.12 3.54 m 22.86** 3.89 m-s 22.89 3.88 vs 26.34 3.38 w-m 23.03 3.86 vs 23.49 3.78 m 26.75 3.33 w-m 23.39 3.80 s 23.93 3.72 vw-w 28.74-29.25* 3.10-3.05 w-m 24.17 3.68 m 24.13 3.68 m 35.72 2.51 vw-w 25.01 3.56 m 24.64 3.61 w 45.29 2.00 w 26.19 3.40 vw-w 24.93 3.57 w 45.62-47.19* 1.99-1.92 vw-w 26.68 3.34 w-m 25.31 3.52 m 28.76 3.10 w-m 26.62 3.35 w 35.72 2.51 vw-w 29.10 3.07 w 45.08 2.01 w 35.72 2.51 vw-w 45.62-47.19* 1.99-1.92 vw-w 45.08 2.01 w 45.62-47.19* 1.99-1.92 vw-w *composite peak consisting of multiple overlapping reflections **Typically a shoulder

In Tables A2 and A3, the term “high” refers to about 60 to about 95 mass-% of the specified component, the term “med” refers to about 25 to about 70 mass-% of the specified component, and the term “low” refers to about 5 to about 40 mass-% of the specified component. Some peaks may be shoulders on more intense peaks, and some peaks may be a composite peak consisting of multiple overlapping reflections.

The UZM-39 material is thermally stable up to a temperature of at least 600° C. and in another embodiment, up to at least 800° C. The UZM-39 material may have a micropore volume as a percentage of total pore volume of greater than 60%.

Characterization of the UZM-39 product by high-resolution scanning electron microscopy shows that the UZM-39 forms in lathes which assemble into rectangular rod particles, often with a starburst cluster arrangement. The starburst cluster rods of UZM-39 can be seen in the scanning electron microscopy results for two particular UZM-39 products in FIG. 7 and in FIG. 8.

UZM-39 is a coherently grown composite structure of TUN and IMF zeotypes. By coherently grown composite structure is meant that both structures are present in a major portion of the crystals in a given sample. This coherently grown composite structure is possible when the two zeotypic structures have nearly identical spacial arrangements of atoms along at least a planar projection of their crystal structure and possess similar pore topologies. FIG. 9 shows a wireframe representation of the TUN framework in the AC plane (left). Each vertex is a tetrahedral site (or T-site) and in the middle of each stick is a corner-shared oxygen atom. A wireframe representation of the IMF framework in the AB plane is shown on the right of FIG. 9. Along these projections, both the TUN and IMF zeotypes contain nearly identical projections of chains of 5-rings connected by 6-rings and 10-rings which form channels running perpendicular to the plane.

As both the TUN and IMF zeotypes are 3-dimensional 10-ring zeolites and have nearly identical projections in one plane, the two structures can thereby coherently grow off crystals of the other structure with interfaces at the compatible planes to form a coherently grown composite structure.

A coherently grown composite structure is not a physical mixture of the two molecular sieves. Electron diffraction, transmission electron microscopy and x-ray diffraction analysis are employed to show that a material is a coherently grown composite structure instead of a physical mixture. Usually the combination of electron diffraction and TEM imaging is most definitive in determining whether one has produced a coherently grown composite structure because it provides direct evidence of the existence of both structures within one crystal.

Since the coherently grown composite structure zeolites of this invention can have varying amounts of the two structure types, it is to be understood that the relative intensity and line width of some of the diffraction lines will vary depending on the amount of each structure present in the coherently grown composite structure. Although the degree of variation in the x-ray powder diffraction patterns is theoretically predictable for specific structures, the more likely mode of a coherently grown composite structure is random in nature and therefore difficult to predict without the use of large hypothetical models as bases for calculation.

Unlike a physical mixture of TNU-9 and IM-5, transmission electron microscopy (TEM) analysis using high resolution imaging and computed optical diffractograms shows that UZM-39 is comprised of a coherently grown composite structure of TUN and IMF zeotypes.

In FIG. 10, TEM analysis of a cross sectioned rod particle from the product of Example 17 shows that areas with TUN and IMF structure occur as coherent sub-regions within an effectively single-crystalline zeolite particle. On the left side of FIG. 11, electron diffraction analysis of the left side of the particle shown in FIG. 10 shows an electron diffraction pattern which can be indexed to the 002 plane of TUN. On the right side of FIG. 11, the electron diffraction pattern from the right side of the particle shown in FIG. 10 is shown. This pattern can be indexed to the 060 plane of IMF. The TUN regions and IMF regions are coherently aligned such that the [010]_(TUN) zone axis and the [001]_(IMF) zone axis are parallel to each other and there is continuity of crystal planes of type (002)_(TUN) and (060)_(IMF), where the indexing is referred to monoclinic C_(2/m) and orthorhombic C_(mem) unit cells for TUN and IMF respectively (details of structures found on IZA website). In spite of the presence of the two zeotypes in different portions of the particle, the image does not show any distinct boundary delineating separate crystals of TUN and IMF, indicating that the particle is a coherently grown composite.

Additionally, UZM-39 zeolite can be characterized by Rietveld analysis of the XRD pattern. Rietveld analysis is a least-squares approach developed by Rietveld (Journal of Applied Crystallography 1969, 2: 65-71) to refine a theoretical line XRD profile until it matches the measured XRD pattern as closely as possible and is the preferred method of deriving structural information from samples such as UZM-39 which contain strongly overlapping reflections. It is often used to quantify the amounts of two different phases in a XRD diffractogram. The accuracy of the Rietveld method is determined by parameters such as crystallite size (peak broadening), peak shape function, lattice unit cell constants and background fits. For the samples shown in the examples, applicants have determined the error in the reported value to be ±5% under the conditions used. Applicants have also determined that the Rietveld model used was unable to quantify the amounts of minority composite structure phase components at values less than 10%, but visually, amounts of the minority components can be seen at levels greater than 5% by comparing against the model patterns. Table 1 shows Rietveld refinement results on various UZM-39 samples from the examples and shows that UZM-39 contains greater than 0 and less than 100 wt. % IMF zeotype and less than 100 wt. % and greater than 0 wt. % TUN zeotype. In another embodiment, UZM-39 contains greater than 5 and less than 95 wt. % IMF zeotype and less than 95 wt. % and greater than 5 wt. % TUN zeotype, and in yet another embodiment, UZM-39 contains greater than 10 and less than 90 wt. % IMF zeotype and less than 90 wt. % and greater than 10 wt. % TUN zeotype. As can be seen in Table 1 and examples, a wide range of coherently grown composite structures are possible by modifying the synthesis conditions.

As synthesized, the UZM-39 material will contain some exchangeable or charge balancing cations in its pores. These exchangeable cations can be exchanged for other cations, or in the case of organic cations, they can be removed by heating under controlled conditions. It is also possible to remove some organic cations from the UZM-39 zeolite directly by ion exchange. The UZM-39 zeolite may be modified in many ways to tailor it for use in a particular application. Modifications include calcination, ion-exchange, steaming, various acid extractions, ammonium hexafluorosilicate treatment, or any combination thereof, as outlined for the case of UZM-4M in U.S. Pat. No. 6,776,975 B1 which is incorporated by reference in its entirety. Conditions may be more severe than shown in U.S. Pat. No. 6,776,975. Properties that are modified include porosity, adsorption, Si/Al ratio, acidity, thermal stability, and the like.

After calcination, ion-exchange and calcination and on an anhydrous basis, the microporous crystalline zeolite UZM-39 has a three-dimensional framework of at least AlO₂ and SiO₂ tetrahedral units and an empirical composition in the hydrogen form expressed by an empirical formula of M1_(a) ^(N+)Al_((1-x))E_(x)Si_(y′)O_(z″) where M1 is at least one exchangeable cation selected from the group consisting of alkali, alkaline earth metals, rare earth metals, ammonium ion, hydrogen ion and combinations thereof, “a” is the mole ratio of M1 to (Al+E) and varies from about 0.05 to about 50, “N” is the weighted average valence of M1 and has a value of about +1 to about +3, E is an element selected from the group consisting of gallium, iron, boron, and combinations thereof, x is the mole fraction of E and varies from 0 to 1.0, y′ is the mole ratio of Si to (Al+E) and varies from greater than about 9 to virtually pure silica and z″ is the mole ratio of O to (Al+E) and has a value determined by the equation: z″=(a·N+3+4·y′)/2

In the hydrogen form, after calcination, ion-exchange and calcination to remove NH₃, UZM-39 displays the XRD pattern shown in Table B1-B3. Those peaks characteristic of UZM-39 are shown in Tables B1-B3 for various coherently grown composite structures. Additional peaks, particularly those of very weak intensity, may also be present. All peaks of medium or higher intensity present in the UZM-39 family of coherently grown composite structures are represented in at least Tables B3.

Table B1 contains selected d-spacings and relative intensities of the hydrogen form of UZM-39 X-ray diffraction pattern. The relative intensities are shown as a range covering UZM-39 materials with varying relative amounts of TUN and IMF zeotypes.

TABLE B1 2θ d (Å) I/Io % 7.11-7.16 12.42-12.25 vw-m  7.5-8.1* 11.78-10.91 m-s 8.84 10.00 m-s 9.06-9.08 9.75-9.73 w-m 9.24 9.56 vw-m 12.46-12.53 7.10-7.06 w-m 22.56 3.94 vw-m 22.75-23.2 3.90-3.83 vs 23.40 3.80 m-s 24.12-24.23 3.69-3.67 w-m 24.92-25.37 3.57-3.51 m 28.71-29.27 3.11-3.05 w-m 45.32-45.36 2.00 w *composite peak consisting of multiple overlapping reflections

The zeolite may be further characterized by the x-ray diffraction pattern having at least the d-spacings and intensities set forth in Table B2 where the d-spacings and intensities are provided at different relative concentrations of the components of the coherently grown composite structure.

TABLE B2 A B C high TUN, low IMF med TUN, med IMF low TUN, high IMF 2-Theta d(†) I/Io % 2-Theta d(†) I/Io % 2-Theta d(†) I/Io % 7.12 12.40 w-m 7.11 12.42 w-m 7.16 12.25 vw-w 7.5-8.1* 11.78-10.91 m 7.5-8.1* 11.78-10.91 m-s 7.5-8.1* 11.78-10.91 m-s 8.84 10.00 m-s 8.84 10.00 m-s 8.84 10.00 m-s 9.06 9.75 m 9.08 9.73 m 9.06** 9.75 w 9.24** 9.56 vw-w 9.24 9.56 m 9.24 9.56 m 12.53 7.06 w 12.48 7.09 m 12.46 7.10 m 22.89 3.88 vs 22.56** 3.94 w-m 22.56 3.94 w-m 23.40 3.80 m 22.75-23.2* 3.90-3.83 vs 23.06 3.85 vs 24.23 3.67 w-m 23.40 3.80 s 23.40 3.80 s 25.22 3.53 m 24.17 3.68 m 24.12 3.69 m 29.08 3.07 w-m 24.92-25.37* 3.57-3.51 m 25.06 3.55 m 45.36 2.00 w 28.71-29.27* 3.11-3.05 w-m 28.82 3.10 w-m 45.34 2.00 w 45.32 2.00 w *composite peak consisting of multiple overlapping reflections **Typically a shoulder

The zeolite may be yet further characterized by the x-ray diffraction pattern having at least the d-spacings and intensities set forth in Table B3 where the d-spacings and intensities are provided at different relative concentrations of the components of the coherently grown composite structure.

TABLE B3 I II III high TUN, low IMF med TUN, med IMF low TUN, high IMF 2-Theta d(†) I/Io % 2-Theta d(†) I/Io % 2-Theta d(†) I/Io % 7.12 12.40 w-m 7.11 12.42 w-m 7.16 12.25 vw-w 7.5-8.1* 11.78-10.91 m 7.5-8.1* 11.78-10.91 m-s 7.5-8.1* 11.78-10.91 m-s 8.84 10.00 m-s 8.84 10.00 m-s 8.84 10.00 m-s 9.06 9.75 m 9.08 9.73 m 9.06** 9.75 w 9.24** 9.56 vw-w 9.24 9.56 m 9.24 9.56 m 12.53 7.06 w 11.76 7.52 vw-w 11.76 7.52 vw-w 14.38 6.15 w 12.48 7.09 m 12.46 7.10 m 14.64 6.05 vw 14.38 6.15 vw-w 14.38 6.15 vw 15.26 5.80 vw-w 14.64 6.05 vw-w 14.64 6.05 w 15.52 5.70 vw 15.26 5.80 w 15.26 5.80 w 16.46 5.38 vw 15.52 5.70 w-m 15.52 5.70 w-m 17.72 5.00 w 16.50 5.37 vw-w 16.58 5.34 w 22.56** 3.94 vw-w 17.72 5.00 w-m 17.72 5.00 w-m 22.89 3.88 vs 18.64 4.76 vw-w 18.64 4.76 w 23.06** 3.85 w-m 22.56** 3.94 w-m 22.56 3.94 w-m 23.40 3.80 m 22.75-23.2* 3.90-3.83 vs 23.06 3.85 vs 23.82 3.73 w-m 23.40 3.80 s 23.40 3.80 s 24.23 3.67 w-m 24.17 3.68 m 24.12 3.69 m 24.70 3.60 w-m 24.70 3.60 w-m 25.06 3.55 m 25.22 3.53 m 24.92-25.37* 3.57-3.51 m 26.16 3.40 vw-w 26.51 3.36 w-m 26.32 3.38 w 26.74 3.33 w-m 29.08 3.07 w-m 26.76 3.33 w-m 28.82 3.10 w-m 35.86 2.50 vw-w 28.71-29.27* 3.11-3.05 w-m 30.12 2.96 w 45.36 2.00 w 30.13 2.96 vw-w 35.86 2.50 vw-w 45.66-47.37* 1.98-1.91 vw-w 35.86 2.50 vw-w 45.32 2.00 w 45.34 2.00 w 45.66-47.37* 1.98-1.91 vw-w 45.66-47.37* 1.98-1.91 vw-w *composite peak consisting of multiple overlapping reflections **Typically a shoulder

In Tables B2 and B3, the term “high” refers to about 60 to about 95 mass-% of the specified component, the term “med” refers to about 25 to about 70 mass-% of the specified component, and the term “low” refers to about 5 to about 40 mass-% of the specified component. Some peaks may be shoulders on more intense peaks, and some peaks may be a composite peak consisting of multiple overlapping reflections.

After acid treating, such as exposure to HNO₃ or H₂SiF₆, and on an anhydrous basis, the microporous crystalline zeolite UZM-39 has a three-dimensional framework of at least AlO₂ and SiO₂ tetrahedral units and an empirical composition in the acid treated form expressed by an empirical formula of M1_(a) ^(N+)Al_((1-x))E_(x)Si_(y′)O_(z″) where M1 is at least one exchangeable cation selected from the group consisting of alkali, alkaline earth metals, rare earth metals, ammonium ion, hydrogen ion and combinations thereof, “a” is the mole ratio of M1 to (Al+E) and varies from about 0.05 to about 50, “N” is the weighted average valence of M1 and has a value of about +1 to about +3, E is an element selected from the group consisting of gallium, iron, boron, and combinations thereof, x is the mole fraction of E and varies from 0 to 1.0, y′ is the mole ratio of Si to (Al+E) and varies from greater than about 9 to virtually pure silica and z″ is the mole ratio of O to (Al+E) and has a value determined by the equation: z″=(a·N+3+4·y′)/2

Similar to the as-synthesized material, the modified UZM-39 materials are thermally stable up to a temperature of at least 600° C. and in another embodiment, up to at least 800° C. and may have a micropore volume as a percentage of total pore volume of greater than 60%.

By virtually pure silica is meant that virtually all the aluminum and/or the E metals have been removed from the framework. It is well known that it is virtually impossible to remove all the aluminum and/or E metal. Numerically, a zeolite is virtually pure silica when y′ has a value of at least 3,000, preferably 10,000 and most preferably 20,000. Thus, ranges for y′ are from 9 to 3,000; from greater than 20 to about 3,000; from 9 to 10,000; from greater than 20 to about 10,000; from 9 to 20,000; and from greater than 20 to about 20,000.

In specifying the proportions of the zeolite starting material or adsorption properties of the zeolite product and the like herein, the “anhydrous state” of the zeolite will be intended unless otherwise stated. The term “anhydrous state” is employed herein to refer to a zeolite substantially devoid of both physically adsorbed and chemically adsorbed water.

The UZM-39 zeolite may be used as the catalyst in processes to produce low oxygen biomass-derived pyrolysis oils. The low oxygen biomass-derived pyrolysis oils produced are substantially fully hydrocarbon products (i.e., products comprising only hydrogen and carbon atoms) making them more suitable for processing into biofuels and chemicals. The methods comprise pyrolyzing carbonaceous biomass feedstock in the presence of the UZM-39 catalyst whereby oxygenated hydrocarbons produced as pyrolysis intermediates are substantially deoxygenated to yield substantially fully hydrocarbon pyrolysis gases, a condensable portion of which is condensed into low oxygen-biomass derived pyrolysis oil. “Hydrocarbons” as used herein are organic compounds that contain principally hydrogen and carbon, i.e., “hydrocarbons” are oxygen-free. “Hydrocarbons” include both aromatic and non-aromatic hydrocarbons. Exemplary aromatic hydrocarbons include benzene, toluene, ethylbenzene, p-xylene, and o-xylene. “Oxygenated hydrocarbons” as used herein are organic compounds containing hydrogen, carbon, and oxygen. Exemplary oxygenated hydrocarbons produced from pyrolysis include carboxylic acids such as acetic acid, phenols, cresols, and aldehydes such as furfural, levoglucosan, etc. It should be appreciated that while the oil produced according to exemplary embodiments of the present invention is generally described herein as a “low oxygen biomass-derived pyrolysis oil”, this term generally includes any oil produced having a lower oxygen concentration than conventional biomass-derived pyrolysis oil. Conventional biomass-derived pyrolysis oil can contain over 40% by weight oxygen from these oxygenated hydrocarbons and typically has high acidity (with a low pH and high total acid number (TAN)) making it corrosive to storage, pipes, and downstream equipment, with low energy density and susceptibility to increased viscosity over time. Conventional biomass-derived pyrolysis oil typically has a pH of <3 and a TAN>150. The term “low oxygen biomass-derived pyrolysis oil” includes oil having no oxygen.

The zeolite as outlined above, or a modification thereof, maybe in a composite with commonly known binders. The UZM-39 preferably is mixed with a binder for convenient formation of catalyst particles in a proportion of about 5 to 100 mass % UZM-39 zeolite and 0 to 95 mass-% binder, with the UZM-39 zeolite preferably comprising from about 10 to 90 mass-% of the composite. The binder should preferably be porous, have a surface area of about 5 to about 800 ^(m2)/g, and be relatively refractory to the conditions utilized in the catalytic pyrolysis process. Non-limiting examples of binders are alumina, titania, zirconia, zinc oxide, magnesia, boria, silica-alumina, silica-magnesia, chromia-alumina, alumina-boria, aluminophosphates, silica-zirconia, silica, silica gel, and clays. Preferred binders are amorphous silica and alumina, including gamma-, eta-, and theta-alumina, with gamma- and eta-alumina being especially preferred.

The zeolite with or without a binder can be formed into various shapes such as pills, pellets, extrudates, spheres, etc. Preferred shapes are extrudates and spheres. Extrudates are prepared by conventional means which involves mixing of the composition either before or after adding metallic components, with the binder and a suitable peptizing agent to form a homogeneous dough or thick paste having the correct moisture content to allow for the formation of extrudates with acceptable integrity to withstand direct calcination. The dough then is extruded through a die to give the shaped extrudate. A multitude of different extrudate shapes are possible, including, but not limited to, cylinders, cloverleaf, dumbbell and symmetrical and asymmetrical polylobates. It is also within the scope of this invention that the extrudates may be further shaped to any desired form, such as spheres, by any means known to the art.

Spheres can be prepared by the well known oil-drop method which is described in U.S. Pat. No. 2,620,314 which is incorporated by reference. The method involves dropping a mixture of zeolite, and for example, alumina sol, and gelling agent into an oil bath maintained at elevated temperatures. The droplets of the mixture remain in the oil bath until they set and form hydrogel spheres. The spheres are then continuously withdrawn from the oil bath and typically subjected to specific aging treatments in oil and an ammoniacal solution to further improve their physical characteristics. The resulting aged and gelled particles are then washed and dried at a relatively low temperature of about 50 to about 200° C. and subjected to a calcination procedure at a temperature of about 450 to about 700° C. for a period of about 1 to about 20 hours. This treatment effects conversion of the hydrogel to the corresponding matrix.

One embodiment of the invention of a process for producing low oxygen biomass-derived pyrolysis oil begins by introducing carbonaceous biomass feedstock (hereinafter “biomass”) into a pyrolysis reactor and pyrolyzing the biomass in the presence of the UZM-39 catalyst. Various types of biomass may be pyrolyzed. Virtually any form of biomass can be considered for pyrolysis to produce biomass-derived pyrolysis oil. Biomass-derived pyrolysis oil may be derived from biomass material such as wood, agricultural wastes/residues, nuts and seeds, algae, grasses, forestry byproducts, cellulose and lignin, municipal waste, construction/demolition debris, or the like. The moisture in the biomass may be reduced by known drying methods prior to introduction into the pyrolysis reactor. Grinding of the biomass may also be performed prior to pyrolysis. The step of pyrolyzing the carbonaceous biomass feedstock in the presence of the UZM-39 catalyst comprises contacting the carbonaceous biomass feedstock and/or pyrolysis gases with the UZM-39 catalyst.

The pyrolysis process produces a carbon-containing solid (char), and pyrolysis gases comprising a variety of oxygenated hydrocarbons, heavy hydrocarbons which include partially depolymerized biomass and light (C₁-C₄) hydrocarbons, carbon oxides such as carbon dioxide and carbon monoxide (collectively “carbon oxides”), hydrogen gas, and steam. The pyrolysis gases comprise a condensable portion (vapors) and a non-condensable portion as hereinafter described. The oxygenated hydrocarbons include carboxylic acids, phenols, cresols, aldehydes, etc. that may contribute to the thermal instability and corrosivity of conventional pyrolysis products.

At pyrolysis temperatures of about 300° C. to about 800° C., the UZM-39 catalyst catalyzes a deoxygenation reaction converting at least a portion of the biomass into hydrocarbons. The biomass is first pyrolyzed into oxygenated hydrocarbons. The oxygen contained in the oxygenated hydrocarbons is then removed as carbon oxides and water. The oxygenated hydrocarbons are substantially deoxygenated by the UZM-39 catalyst; however, less than complete deoxygenation may occur. Any oxygenated hydrocarbons remaining in the pyrolysis gases after pyrolysis are referred to herein as “residual oxygenated hydrocarbons.” Residual oxygenated hydrocarbons having relatively high carbon/oxygen ratio may also be desirable. The pyrolysis and deoxygenation occur substantially simultaneously in the pyrolysis reactor.

The biomass may be pyrolyzed using various pyrolysis methods including fast pyrolysis and other pyrolysis methods such as vacuum pyrolysis, slow pyrolysis, and others. Fast pyrolysis includes rapidly imparting a relatively high temperature to feedstocks for a very short residence time, typically about 0.5 seconds to about 0.5 minutes, and then rapidly reducing the temperature of the pyrolysis products before chemical equilibrium can occur. By this approach, the complex structures of the biomass are broken into reactive chemical fragments that are initially formed by depolymerization and volatilization reactions, but do not persist for any significant length of time. Fast pyrolysis is an intense, short duration process that can be carried out in a variety of pyrolysis reactors such as fixed bed pyrolysis reactors, fluidized bed pyrolysis reactors, circulating fluidized bed reactors (CFBR), or other pyrolysis reactors capable of fast pyrolysis as known in the art. For example, in an exemplary fluidized bed pyrolysis reactor, carbonaceous biomass feedstock is thermally converted (i.e., pyrolyzed) at pyrolysis temperatures (about 300° C. to about 800° C.) in the presence of a heat transfer medium.

The heat transfer medium comprises the UZM-39 catalyst or a combination of the UZM-39 catalyst and an inert solid such as sand. The UZM-39 catalyst, with or without inorganic inert solids such as sand, serve as the heat transfer medium for a fast pyrolysis process as previously described. The particle size of the heat transfer medium is typically 40-500 micron. However, the heat required to drive the pyrolysis process may be derived from other sources (e.g., an organic heat source such as char) as well known in the art. The heat transfer medium may be provided in a fluidized state and maintained at a temperature suitable for pyrolysis to pyrolyze the carbonaceous biomass feedstock. In one embodiment, the ratio of heat transfer medium to biomass is greater than 8 by mass and preferably greater than 12. The ratio of UZM-39 catalyst to biomass is from 0.1 to 200 by mass. Preferably, the ratio of catalyst to biomass is from 0.1 to 50 by mass and can be from 0.1 to 12 by mass. In one embodiment, the heat transfer medium may be fluidized by a fluidizing gas. Flue gases from the pyrolysis reactor or a non-condensable portion of the pyrolysis gases may be compressed and fed into the pyrolysis reactor as a fluidizing gas for bed fluidization. The heat transfer medium forms a fluidized bed within the pyrolysis reactor.

Once the carbonaceous biomass feedstock has been pyrolyzed, solid carbon-containing char and pyrolysis gases comprising the condensable portion (vapors) and the non-condensable portion exit the pyrolysis reactor 20. The solid char may be separated from the pyrolysis gases. The spent heat transfer medium comprising the UZM-39 catalyst, the inert solids, or both, are separated from the pyrolysis gases and may be regenerated. The spent heat transfer medium and solid char may also be concurrently separated from the pyrolysis gases.

A circulating fluidizing bed reactor (CFBR) is a preferred pyrolysis reactor. One such circulating bed transport reactor for use in fast pyrolysis is described, for example, in U.S. Pat. No. 5,961,786. There, the carbonaceous biomass feedstock, typically less than 6 mm in size, essentially oxygen-free fluidizing gas, and a heat transfer medium are rapidly mixed in a thermal mixing section of a pyrolysis reactor base section, then transported upward through an entrained-bed tubular reactor. After fast pyrolysis, a cyclonic hot solids recirculation system separates the solid heat transfer medium from the non-condensable pyrolysis gases and condensable pyrolysis gases (vapors) and returns the heat transfer medium to the mixing section to be used again. The heat required to drive the pyrolysis process is transferred to the mixing and reaction zones principally by recirculated heat transfer medium. Typically, there is no oxidation (combustion) occurring in the mixing and reaction zones to supply direct process heat as preferably there is very little oxygen present. Direct or indirect combustion of char or gas, or externally supplied fuel, or indirect electrical resistance heating may be employed to heat the recirculated heat transfer medium before injection into the mixing section. It is to be understood that the fast pyrolysis methods described above are exemplary. In addition, while mixing of the carbonaceous biomass feedstock with a heat transfer medium in the mixing section of a pyrolysis reactor has been described, the carbonaceous biomass feedstock may be mixed with the heat transfer medium prior to introduction into the pyrolysis reactor. The catalyst may alternatively be finely ground and used in a Fluid Catalytic Cracking (FCC) unit fed with the biomass.

The process continues with condensing the condensable portion (vapors) of the pyrolysis gases. The pyrolysis gases are passed to a condenser or series of condensers with the non-condensable portion. The non-condensable portion may be recovered for other uses. The non-condensable portion of the pyrolysis gases comprises hydrogen gas, methane, and carbon oxides which may be separated from each other by methods well known in the art. Ash-laden flue gas from the pyrolysis reactor is transferred from the reheater to a separation apparatus for separation of the ash from the flue gas. The flue gas may be recycled to the pyrolysis reactor as the fluidizing gas for the pyrolysis reactor. The condensable portion (vapors) of the pyrolysis gases comprising hydrocarbons and any residual oxygenated hydrocarbons is condensed in a condenser into low oxygen biomass-derived pyrolysis oil having substantially improved energy density, lower total acid number (TAN), and higher thermal stability than conventional biomass-derived pyrolysis oil. The low oxygen biomass-derived pyrolysis oil has potential for use as a biofuel substantially eliminating the need for secondary upgrading to remove oxygen therefrom as is needed with conventional biomass-derived pyrolysis oils. Alternatively, the low oxygen biomass-derived pyrolysis oil can be used as to produce aromatic chemicals. In an embodiment, the selectivity to aromatic compounds within the condensable portion of the pyrolysis gases is greater than 33% by weight and possibly greater than 50% by weight. The yield of aromatic compounds is greater than 2% by weight on biomass and preferably greater than 3%.

Pyrolyzing the carbonaceous biomass feedstock in the presence of the UZM-39 catalyst results in spent catalyst. The spent catalyst may be regenerated and recycled when its activity has dropped below a desired level. The time in which the catalyst will maintain its activity varies. Gradually, there may be a loss of catalyst activity due to fouling (e.g., due to carbon deposits formed on the catalyst). The spent UZM-39 zeolite may be heated under such conditions as to remove the carbonaceous materials from a surface thereof. The regenerated catalyst then may be recirculated to the pyrolysis reactor.

The following examples are presented in illustration of this invention and are not intended as undue limitations on the generally broad scope of the invention as set out in the appended claims.

The structure of the UZM-39 zeolite of this invention was determined by x-ray analysis. The x-ray patterns presented in the following examples were obtained using standard x-ray powder diffraction techniques. The radiation source was a high-intensity, x-ray tube operated at 45 kV and 35 ma. The diffraction pattern from the copper K-alpha radiation was obtained by appropriate computer based techniques. Flat compressed powder samples were continuously scanned at 2° to 56° (2θ). Interplanar spacings (d) in Angstrom units were obtained from the position of the diffraction peaks expressed as θ where θ is the Bragg angle as observed from digitized data. Intensities were determined from the integrated area of diffraction peaks after subtracting background, “I_(o)” being the intensity of the strongest line or peak, and “I” being the intensity of each of the other peaks.

As will be understood by those skilled in the art the determination of the parameter 2θ is subject to both human and mechanical error, which in combination can impose an uncertainty of about ±0.4° on each reported value of 2θ. This uncertainty is, of course, also manifested in the reported values of the d-spacings, which are calculated from the 2θ values. This imprecision is general throughout the art and is not sufficient to preclude the differentiation of the present crystalline materials from each other and from the compositions of the prior art. In some of the x-ray patterns reported, the relative intensities of the d-spacings are indicated by the notations vs, s, m, and w which represent very strong, strong, medium, and weak, respectively. In terms of 100×I/I_(o), the above designations are defined as: vw=<5; w=6-15; m=16-50:s=51-80; and vs=80-100

In certain instances the purity of a synthesized product may be assessed with reference to its x-ray powder diffraction pattern. Thus, for example, if a sample is stated to be pure, it is intended only that the x-ray pattern of the sample is free of lines attributable to crystalline impurities, not that there are no amorphous materials present.

In order to more fully illustrate the invention, the following examples are set forth. It is to be understood that the examples are only by way of illustration and are not intended as an undue limitation on the broad scope of the invention as set forth in the appended claims.

EXAMPLE 1

A sample of UZM-39 was prepared as follows. 6.02 g of NaOH, (97%) was dissolved in 125.49 g water. 0.62 g Al(OH)₃, (29.32 wt.-% Al) was added to the NaOH solution to form a first solution. Separately, 0.24 g of the layered material UZM-8 was stirred into 30.0 g Ludox AS-40 to form a second solution. The second solution was added to the first solution. The mixture was cooled to 0° C.-4° C. Separately, 6.54 g 1,4-dibromobutane, (99 wt.-%) was mixed with 7.65 g 1-methylpyrrolidine, (97 wt.-%) to form a third solution. The third solution was added to the cooled mixture of the first and second solutions to form the final reaction mixture. The final reaction mixture was transferred to a 300 cc stirred autoclave and digested at 160° C. for 144 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD as shown in FIG. 1. Analytical results show this material has the following molar rations: Si/Al of 12.64, Na/Al of 0.116, N/Al of 0.92, C/N of 7.23.

Scanning Electron Microscopy (SEM) revealed crystals of intergrown, square rod morphology in starbursts, approximately 250 to 700 nm along a face of the square with an aspect ratio of from 2:1 to 5:1. The micrograph is shown in FIG. 7. The product was calcined at 550° C. for 3 hrs under air. The XRD pattern of the calcined material is shown in FIG. 2.

COMPARATIVE EXAMPLE 2

The preparation of Example 1 was followed, except that the layered material UZM-8 was not added to the second solution. After 144 hours of stirring at 100 rpm at 160° C., the product was isolated by filtration. The product was identified as analcime by XRD.

COMPARATIVE EXAMPLE 3

6.68 g of NaOH, (97%) was dissolved in 145.44 g water. 2.86 g Al(NO₃)₃.9H₂O (97%) was added to the sodium hydroxide solution. 13.33 g Aerosil 200 was stirred into the mixture. 13.1 g H₂O was added. 7.26 g 1,4-dibromobutane, (99%) and 5.84 g 1-methylpyrrolidine, (97%) were added and the mixture was stirred vigorously for a day. The mixture was divided equally and loaded into eight 45 cc Parr vessels and placed into a rotisserie oven at 160°. The mixture in one of the Parr vessels produced a material at 256 hours identified by XRD as having the TUN structure. Analytical results showed this material to have the following molar ratios, Si/Al of 15.51, Na/Al of 0.12, N/Al of 1.29, and C/N of 6.89. SEM analysis revealed a squat rod cluster morphology, about 300-800 nm in length and with an aspect ratio of about 1.

The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged four times with 1 M ammonium nitrate solution at 75° followed by a calcination at 500° under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis for the calcined, ion-exchanged sample showed 39.2 wt. % Si, 2.34 wt. % Al, <0.005 wt. % Na with a BET surface area of 378 m²/g, pore volume of 0.220 cm³/g, and micropore volume of 0.190 cm³/g.

Analysis of the H⁺-form of this material by Rietveld XRD refinement showed that the material consisted entirely of TUN structure type. TEM analysis confirmed that no coherent growth of IMF crystals occurred.

EXAMPLE 4

6.40 g of NaOH, (97%) was dissolved in 111.88 g water. 1.16 g Al(OH)₃, (29.32 wt.-% Al), was added to the sodium hydroxide solution to create a first solution. Separately, 0.30 g of the layered material (UZM-8) was stirred into 37.5 g Ludox AS-40 to form a second solution. The second solution was added to the first solution and vigorously stirred for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 8.18 g 1,4-dibromobutane, (99 wt.-%) was mixed with 9.56 g 1-methylpyrrolidine, (97 wt.-%) to form a third solution. The third solution was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 144 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 12.07, Na/Al of 0.124, N/Al of 0.90, C/N of 6.85.

EXAMPLE 5

7.19 g of NaOH, (99 wt.-%%) was dissolved in 90.1 g water. 1.56 g Al(OH)₃, (29.32 wt.-% Al), was added to the sodium hydroxide solution to create a first solution. Separately, 0.405 g of the layered material (UZM-8) was stirred into 50.62 g Ludox AS-40 to form a second solution. The second solution was added to the first solution and vigorously stirred for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 11.04 g 1,4-dibromobutane, (99 wt.-%), was mixed with 12.90 g 1-methylpyrrolidine, (97 wt.-%) to form a third solution. The third solution was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred for 5 minutes and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 144 hours with stirring at 100 rpm. 16.5 g of the product was isolated by filtration. The product was identified by XRD to be UZM-39 with a very slight MOR impurity. Analytical results showed this material to have the following molar ratios, Si/Al of 14.14, Na/Al of 0.16, N/Al of 1.02, C/N of 7.33.

EXAMPLE 6

37.62 g of NaOH, (97 wt.-%) was dissolved in 600 g water to create a sodium hydroxide solution. 6.96 g Al(OH)₃ (29.32 mass % Al) was added to the sodium hydroxide solution to create a first solution. Separately, 1.80 g of the layered material (UZM-8) was stirred into 225 g Ludox AS-40 to form a second solution. The second solution was added to the first solution and vigorously stirred for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 49.08 g 1,4-dibromobutane (99 wt.-%) was mixed with 57.36 g 1-methylpyrrolidine (97 wt.-%) for 1-5 minutes to form a third solution. The third solution was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred for 5 minutes and transferred to a 2 liter stirred autoclave. The final reaction mixture was digested at 160° C. for 144 hours with stirring at 250 rpm. The product was isolated by filtration. The product was identified by XRD as UZM-39. Analytical results showed this material to have the following molar ratios, Si/Al of 11.62, Na/Al of 0.12, N/Al of 0.88, C/N of 7.36.

The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged four times with 1 M ammonium nitrate solution at 75° followed by a calcination at 500° C. under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis of the H⁺ form of this material by Rietveld XRD refinement gave the results shown in Table 1.

EXAMPLE 7

505.68 g of NaOH, (99 wt.-%) was dissolved in 10542 g water. 52.08 g Al(OH)₃, (29.3 wt.-% Al), was added to the sodium hydroxide solution to create a first solution. Separately, 20.16 g of the layered material (UZM-8) was stirred into 2520 g Ludox AS-40 to form a second solution. The second solution was added to the first solution and vigorously stirred for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 549.36 g 1,4-dibromobutane (99 wt.-%) was mixed with 642.6 g 1-methylpyrrolidine, (97 wt.-%), for 3-5 minutes to form a third solution. The third solution was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred for 5 minutes and pumped into a 5 gallon stirred autoclave. The final reaction mixture was digested at 160° C. for 150 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified by XRD as UZM-39. Analytical results showed this material to have the following molar ratios, Si/Al=13.35, Na/Al=0.087, N/Al=0.96, C/N=7.12.

EXAMPLE 8

The preparation of Example 4 was followed except that UZM-8 was replaced with 0.30 g UZM-26. The product was identified by XRD as UZM-39. Analytical results showed this material to have the following molar ratios: Si/Al=12.88, Na/Al=0.25, N/Al=0.88, C/N=7.31.

EXAMPLE 9

6.27 g of NaOH, (99%), was dissolved in 111.88 g water to create a sodium hydroxide solution. 1.16 g Al(OH)₃ (29.32 mass % Al) was added to the sodium hydroxide solution to create a first solution. 37.5 g Ludox AS-40 and then 0.22 g of the layered material UZM-5 were added to the first solution. The first solution was vigorously stirred for 1-2 hours. The first solution was cooled to 0° C.-4° C. Separately, 8.18 g 1,4-dibromobutane (99%) was mixed with 9.56 g 1-methylpyrrolidine (97%) for 1-5 minutes to form a second solution. The second solution was added to the cooled first solution to create the final reaction mixture. The final reaction mixture was vigorously stirred for approximately 5 minutes and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 144 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified by XRD as UZM-39 with a very small EUO or NES contaminant.

COMPARATIVE EXAMPLE 10

This example is identical to example 4 except that UZM-8 was replaced with 0.30 g UZM-39. The product was identified as a composition comprising MTW, UZM-39, ANA and MOR.

EXAMPLE 11

6.27 g of NaOH, (97 wt.-%) was dissolved in 111.88 g water. 1.16 g Al(OH)₃, (29.32 wt. % Al), was added to the sodium hydroxide solution to create a first solution. Separately, 0.30 g of the layered material (UZM-8) was stirred into 37.5 g Ludox AS-40 to form a second solution. The second solution was added to the first solution and vigorously stirred for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 12.27 g 1,4-dibromobutane (99 wt.-%) was mixed with 14.34 g 1-methylpyrrolidine (97 wt.-%) to form a third solution. The third solution was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 144 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 with an ESV impurity by XRD. Analytical results showed this material to have the following molar ratios, Si/Al=13.17, Na/Al=0.126, N/Al=1.03, C/N=7.22.

EXAMPLE 12

The procedure of Example 4 was followed except 9.56 g 1-methylpyrrolidine, (97 wt.-%), was replaced with 8.05 g dimethylethylamine, (97 wt.-%). The product was identified as a composition comprising mordenite and UZM-39.

EXAMPLE 13

6.27 g of NaOH (99 wt.-%) was dissolved in 111.88 g water. 1.16 g Al(OH)₃ (29.32 wt.-% Al) was added to the sodium hydroxide solution to create a first solution. 0.30 g of the layered material UZM-8 and 37.5 g Ludox AS-40 were added to the first solution. The first solution was vigorously stirred for 1-2 hours. The first solution was cooled to 0° C.-4° C. Separately, 4.02 g dimethylethylamine (97 wt.-%) was mixed with 4.78 g 1-methylpyrrolidine (97 wt.-%) for 1-2 minutes to form an amine solution. 8.18 g 1,4-dibromobutane (99 wt.-%) was added to the amine solution and then mixed for 1-2 minutes to form a second solution. The second solution was added to the cooled first solution to create the final reaction mixture. The final reaction mixture was vigorously stirred for approximately 5 minutes and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 192 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al=12.42, Na/Al=0.175, N/Al=0.91, C/N=6.92.

The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged four times with 1 M ammonium nitrate solution at 75° followed by a calcination at 500° C. under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis for the calcined, ion-exchanged sample shows 38.7% Si, 2.97% Al, 0.0089% Na with a BET surface area of 375 m²/g, pore volume of 0.238 cm³/g, and micropore volume of 0.184 cm³/g. Analysis of the H⁺ form of this material by Rietveld XRD refinement gave the results shown in Table 1.

EXAMPLE 14

6.21 g of NaOH, (99%), was dissolved in 111.88 g water to create a sodium hydroxide solution. 1.16 g Al(OH)₃ (29.32 wt.-% Al) was added to the sodium hydroxide solution to create a first solution. 0.30 g of the layered material (UZM-8) and 37.5 g Ludox AS-40 were added to the first solution. The first solution was vigorously stirred for 1-2 hours. The first solution was cooled to 0° C.-4° C. Separately, 8.18 g 1,4-dibromobutane (99 wt.-%) was mixed with 9.56 g 1-methylpyrrolidine (97 wt.-%) for 1-5 minutes to form a second solution. The second solution was added to the cooled first solution to create the final reaction mixture. The final reaction mixture was vigorously stirred for approximately 5 minutes and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 170° C. for 96 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 12.76, Na/Al of 0.116, N/Al of 0.94, C/N of 6.98.

EXAMPLE 15

6.21 g of NaOH, (99%), was dissolved in 111.88 g water to create a sodium hydroxide solution. 1.16 g Al(OH)₃ (29.32 wt.-% Al) was added to the sodium hydroxide solution to create a first solution. 0.30 g of the layered material (UZM-8) and 37.5 g Ludox AS-40 were added to the first solution. The first solution was vigorously stirred for 1-2 hours. The first solution was cooled to 0° C.-4° C. Separately, 8.18 g 1,4-dibromobutane (99 wt.-%) was mixed with 9.56 g 1-methylpyrrolidine (97 wt.-%) for 1-5 minutes to form a second solution. The second solution was added to the cooled first solution to create the final reaction mixture. The final reaction mixture was vigorously stirred for approximately 5 minutes and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 175° C. for 44 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 12.97, Na/Al of 0.20, N/Al of 0.95, C/N of 6.98.

EXAMPLE 16

5.96 g of NaOH, (97%) and 0.25 g KOH, (86%) were dissolved in 111.88 g water. 1.22 g Al(OH)₃, (27.9 wt.-% Al), was added to the sodium hydroxide solution. 37.5 g Ludox AS-40 and then 0.30 g of the layered material UZM-8 were added to the first solution and stirred vigorously for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 8.18 g 1,4-dibromobutane, (99%) was mixed with 9.56 g 1-methylpyrrolidine, (97%) to form a third mixture. The third mixture was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 144 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. The x-ray diffraction pattern is shown in FIG. 3. Analytical results showed this material to have the following molar ratios, Si/Al of 11.69, Na/Al of 0.137, K/Al of 0.024, N/Al of 0.848, C/N of 7.16.

The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged four times with 1 M ammonium nitrate solution at 75° followed by a calcination at 500° C. under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis for the calcined, ion-exchanged sample shows 39.4% Si, 3.23% Al, 0.011% Na, 0.005% K with a BET surface area of 362 m²/g, pore volume of 0.231 cm³/g, and micropore volume of 0.176 cm³/g. The x-ray diffraction pattern in shown in FIG. 4.

EXAMPLE 17

5.96 g of NaOH, (99%) and 0.50 g KOH, (86%) were dissolved in 111.88 g water. 1.16 g Al(OH)₃, (29.32 wt.-% Al), was added to the sodium hydroxide solution. 37.5 g Ludox AS-40 and then 0.30 g of the layered material UZM-8 were added to the first solution and stirred vigorously for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 4.09 g 1,4-dibromobutane, (99%) was mixed with 11.15 g 1-methylpyrrolidine, (97%) to form a third mixture. The third mixture was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 144 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 11.98, Na/Al of 0.114, K/Al of 0.0375 N/Al of 0.84, C/N of 7.50.

The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged four times with 1 M ammonium nitrate solution at 75° followed by a calcination at 500° C. under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis for the calcined, ion-exchanged sample shows 37.7% Si, 3.01% Al, 0.012% Na, 0.006% K. Analysis of the H⁺ form of this material by Rietveld XRD refinement gave the results shown in Table 1. TEM analysis showed that UZM-39 is a coherently grown composite structure of TUN and IMF zeotypes, the results of which analysis are shown in FIGS. 10 and 11.

EXAMPLE 18

5.64 g of NaOH, (97%) and 1.00 g KOH, (86%) were dissolved in 111.88 g water. 1.22 g Al(OH)₃, (27.9 wt.-% Al), was added to the sodium hydroxide solution. 37.5 g Ludox AS-40 and then 0.30 g of the layered material UZM-8 were added to the first solution and stirred vigorously for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 8.18 g 1,4-dibromobutane, (99%) was mixed with 9.56 g 1-methylpyrrolidine, (97%) to form a third mixture. The third mixture was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 144 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 11.29, Na/Al of 0.078, K/Al of 0.053 N/Al of 0.88, C/N of 6.92. The SEM image of the product is shown in FIG. 8.

The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged four times with 1 M ammonium nitrate solution at 75° followed by a calcination at 500° C. under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis for the calcined, ion-exchanged sample shows 42.6% Si, 3.65% Al, 0.0018% Na, 0.02% K with a BET surface area of 351 m²/g, pore volume of 0.218 cm³/g, and micropore volume of 0.170 cm³/g. Analysis of the H⁺ form of this material by Rietveld XRD refinement gave the results shown in Table 1.

EXAMPLE 19

5.02 g of NaOH, (97%) and 2.00 g KOH, (86%) were dissolved in 111.88 g water. 1.22 g Al(OH)₃, (27.9 wt.-% Al), was added to the sodium hydroxide solution. 37.5 g Ludox AS-40 and then 0.30 g of the layered material UZM-8 were added to the first solution and stirred vigorously for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 8.18 g 1,4-dibromobutane, (99%) was mixed with 9.56 g 1-methylpyrrolidine, (97%) to form a third mixture. The third mixture was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 136 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD with a likely small amount of NES contaminant Analytical results showed this material to have the following molar ratios, Si/Al of 10.99, Na/Al of 0.088, K/Al; of 0.11 N/Al of 0.84, C/N of 7.36.

EXAMPLE 20

5.96 g of NaOH, (99%) was dissolved in 111.88 g water. 1.22 g Al(OH)₃, (27.9 wt.-% Al), was added to the sodium hydroxide solution. Then 0.24 g Mg(OH)₂ (95%), 37.5 g Ludox AS-40, and 0.30 g of the layered material UZM-8 were added in the order listed to the first solution and stirred vigorously for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 8.18 g 1,4-dibromobutane, (99%) was mixed with 9.56 g 1-methylpyrrolidine, (97%) and added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 144 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 12.12, Na/Al of 0.148, Mg/Al of 0.38 N/Al of 0.91, C/N of 6.96.

The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged four times with 1 M ammonium nitrate solution at 75° followed by a calcination at 500° C. under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis for the calcined, ion-exchanged sample shows 39.6% Si, 2.99% Al, 83 ppm Na, 0.14% Mg with a BET surface area of 351 m²/g, pore volume of 0.218 cm³/g, and micropore volume of 0.170 cm³/g.

EXAMPLE 21

5.96 g of NaOH, (99%) and 0.51 g La(OH)₃, (99.9%) were dissolved in 111.88 g water. 1.16 g Al(OH)₃, (29.32 wt.-% Al), was added to the sodium hydroxide solution. 37.5 g Ludox AS-40 and then 0.30 g of the layered material UZM-8 were added to the first solution and stirred vigorously for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 8.18 g 1,4-dibromobutane, (99%) was mixed with 9.56 g 1-methylpyrrolidine, (97%) and added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 168 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 12.22, Na/Al of 0.20, La/Al of 0.18, N/Al of 0.89, C/N of 7.13.

The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged four times with 1 M ammonium nitrate solution at 75° followed by a calcination at 500° C. under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis for the calcined, ion-exchanged sample shows 39.1% Si, 3.06% Al, 60 ppm Na, 0.25% La with a BET surface area of 335 m²/g, pore volume of 0.226 cm³/g, and micropore volume of 0.163 cm³/g.

EXAMPLE 22

3.14 g of NaOH, (97%) was dissolved in 106.41 g water. 1.16 g Al(OH)₃, (29.32 wt.-% Al), was added to the sodium hydroxide solution. 37.5 g Ludox AS-40 and then 0.30 g of the layered material UZM-8 were added to the first solution. Next 26.7 g Na silicate solution (13.2 wt. % Si; 6.76 wt. % Na) is added to the above and stirred vigorously for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 8.18 g 1,4-dibromobutane, (99%) was mixed with 9.56 g 1-methylpyrrolidine, (97%) to form a third mixture. The third mixture was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 224 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 11.75, Na/Al of 0.11, N/Al of 0.90, C/N of 6.99.

The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged three times with 1 M ammonium nitrate solution at 75° followed by a calcination at 500° C. under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis for the calcined, ion-exchanged sample shows 38.8% Si, 3.05% Al, 0.011% Na, with a BET surface area of 364 m²/g, pore volume of 0.273 cm³/g, and micropore volume of 0.174 cm³/g. Analysis of the H⁺ form of this material by Rietveld XRD refinement gave the results shown in Table 1.

EXAMPLE 23

5.33 g of NaOH, (99%) was dissolved in 111.88 g water. 1.16 g Al(OH)₃, (29.32 wt.-% Al), was added to the sodium hydroxide solution. Separately, 0.30 g of Beta zeolite was stirred into 37.5 g Ludox AS-40 to make a second mixture. This second mixture was added to the first solution and stirred vigorously for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 8.89 g 1,5-dibromopentane, (97%) was mixed with 9.56 g 1-methylpyrrolidine, (97%) to form a third mixture. The third mixture was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 256 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 13.24, Na/Al of 0.13, N/Al of 0.91, C/N of 7.21.

The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged three times with 1 M ammonium nitrate solution at 75° followed by a calcination at 500° C. under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis of the H⁺ form of this material by Rietveld XRD refinement gave the results shown in Table 1.

COMPARATIVE EXAMPLE 24

10.8 g of Aerosil 200 was added, while stirring, to a solution of 12.24 g 1,5-bis(N-methylpyrrolidinium)pentane dibromide in 114 g H₂O. A very thick gel was formed. Separately, a solution was made from 60 g H₂O, 3.69 g NaOH (99%), 0.95 g sodium aluminate (26.1% Al by analysis), and 1.86 g NaBr (99%). This second solution was added to the above mixture which thins out a bit. The final mixture was divided equally between 7 45 cc Parr vessels. One vessel, which was digested for 12 days at 170° C. in a rotisserie oven at 15 rpm, yielded a product which was determined by XRD as having the IMF structure. The product was isolated by filtration. The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged four times with 1 M ammonium nitrate solution at 75° followed by a calcination at 500° under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis of the H+-form of this material by Rietveld XRD refinement showed that the material consisted entirely of IMF structure type. TEM analysis confirmed that no coherent growth of TUN crystals occurred.

EXAMPLE 25

31.98 g of NaOH, (99%) was dissolved in 671.3 g water. 6.96 g Al(OH)₃, (29.32 wt.-% Al), was added to the sodium hydroxide solution. Separately, 1.80 g of the layered material UZM-8 was stirred into 225.0 g Ludox AS-40 to make a second mixture. This second mixture was added to the first solution and stirred vigorously for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 53.34 g 1,5-dibromopentane, (97%) was mixed with 57.36 g 1-methylpyrrolidine, (97%) to form a third mixture. The third mixture was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 2 L stirred autoclave. The final reaction mixture was digested at 160° C. for 256 hours with stirring at 250 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 12.30, Na/Al of 0.13, N/Al of 0.92, C/N of 7.51.

The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged three times with 1 M ammonium nitrate solution at 75° followed by a calcination at 500° under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis for the calcined, ion-exchanged sample shows 39.0% Si, 2.93% Al, 0.008% Na. Analysis of the H+-form of this material by Rietveld XRD refinement gave the results shown in Table 1.

EXAMPLE 26

5.76 g of NaOH, (97%) was dissolved in 111.88 g water. 1.22 g Al(OH)₃, (27.9 wt.-% Al), was added to the sodium hydroxide solution. When this became a solution, 37.5 g Ludox AS-40 was added. Next 0.30 g of the layered material UZM-8 was added. The mixture was stirred vigorously for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 0.89 g 1,5-dibromopentane, (97%) was mixed with 7.36 g 1,4-dibromobutane, (99%), then 9.56 g 1-methylpyrrolidine, (97%) was added to form a second mixture. The second mixture was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 176 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 12.15, Na/Al of 0.15, N/Al of 0.90, C/N of 7.59.

The product generated by this synthesis was calcined under flowing air at 600° C. for 6 hours. It was then ion exchanged four times with 1 M ammonium nitrate solution at 75° C. followed by a calcination at 500° C. under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis for the calcined, ion-exchanged sample shows 38.6% Si, 2.85% Al, <0.01% Na. Analysis of the H⁺ form of this material by Rietveld XRD refinement gave the results shown in Table 1.

EXAMPLE 27

5.76 g of NaOH, (97%) was dissolved in 111.88 g water. 1.22 g Al(OH)₃, (27.9 wt.-% Al), was added to the sodium hydroxide solution. When this became a solution, 37.5 g Ludox AS-40 was added. Next, 0.30 g of the layered material UZM-8 was added and the mixture was stirred vigorously for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 1.78 g 1,5-dibromopentane, (97%) was mixed with 6.54 g 1,4-dibromobutane, (99%), then 9.56 g 1-methylpyrrolidine, (97%) was added to form a second mixture. The second mixture was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 176 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 12.24, Na/Al of 0.107, N/Al of 0.93, C/N of 6.91. The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged four times with 1 M ammonium nitrate solution at 75° C. followed by a calcination at 500° C. under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis for the calcined, ion-exchanged sample shows 38.7% Si, 2.98% Al, 158 ppm Na with a BET surface area of 333 m²/g, pore volume of 0.201 cm³/g, and micropore volume of 0.164 cm³/g. Analysis of the H⁺ form of this material by Rietveld XRD refinement gave the results shown in Table 1.

EXAMPLE 28

5.76 g of NaOH, (97%) was dissolved in 111.88 g water. 1.22 g Al(OH)₃, (27.9 wt.-% Al), was added to the sodium hydroxide solution. When this became a solution, 37.5 g Ludox AS-40 was added. Next, 0.30 g of the layered material UZM-8 was added and the mixture was stirred vigorously for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 2.67 g 1,5-dibromopentane, (97%) was mixed with 5.73 g 1,4-dibromobutane, (99%), then 9.56 g 1-methylpyrrolidine, (97%) was added to form a second mixture. The second mixture was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 176 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. The x-ray diffraction pattern is shown in FIG. 5. Analytical results showed this material to have the following molar ratios, Si/Al of 12.15, Na/Al of 0.108, N/Al of 0.86, C/N of 7.68.

The product generated by this synthesis was calcined under flowing air at 600° C. for 6 hours. It was then ion exchanged four times with 1 M ammonium nitrate solution at 75° C. followed by a calcination at 500° under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis for the calcined, ion-exchanged sample shows 38.7% Si, 2.98% Al, 79 ppm Na. The x-ray diffraction pattern is shown in FIG. 6. Analysis of the H⁺ form of this material by Rietveld XRD refinement gave the results shown in Table 1.

EXAMPLE 29

5.80 g of NaOH, (97%) was dissolved in 111.88 g water. 1.16 g Al(OH)₃, (29.32 wt.-% Al), was added to the sodium hydroxide solution. When this became a solution, 37.5 g Ludox AS-40 was added. Next, 0.30 g of the layered material UZM-8 was added and the mixture was stirred vigorously for 1-2 hours. The mixture was cooled to 0° C.-4° C. Separately, 4.45 g 1,5-dibromopentane, (97%) was mixed with 4.09 g 1,4-dibromobutane, (99%), then 9.56 g 1-methylpyrrolidine, (97%) was added to form a second mixture. The second mixture was added to the cooled mixture to create the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 300 cc stirred autoclave. The final reaction mixture was digested at 160° C. for 224 hours with stirring at 100 rpm. The product was isolated by filtration. The product was identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 11.75, Na/Al of 0.13, N/Al of 0.86, C/N of 7.59.

The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion exchanged four times with 1 M ammonium nitrate solution at 75° C. followed by a calcination at 500° C. under air for 2 hours to convert NH₄ ⁺ into H⁺. Analysis for the calcined, ion-exchanged sample shows 40.1% Si, 3.32% Al, 90 ppm Na with a BET surface area of 305 m²/g, pore volume of 0.224 cm³/g, and micropore volume of 0.146 cm³/g. Analysis of the H⁺ form of this material by Rietveld XRD refinement gave the results shown in Table 1.

TABLE 1 Example # % TUN % IMF 3 100 0 6 95 5 13 83 17 17 46 54 18 36.5 63.5 23 24 76 24 0 100 25 19 81 26 58 42 27 30 70 28 13 87 29 8 92

EXAMPLE 30

To determine the quantities of TUN or IMF structure able to be detected in a UZM-39 coherently grown composite structure material, a detection limit study was performed. A series of simulated diffraction patterns were electronically created from the observed diffraction patterns of the H⁺ forms of Example 3 and Example 24 products using JADE XRD analysis software (available from Materials Data Incorporated). Mixture levels ranged from 1% to 99% TUN and were created by scaling the smaller percentage constituent to the required level, adding the patterns and saving the composite pattern.

Rietveld analysis was able to quantify the level of IMF in the UZM-39 coherently grown composite structure at the 10% or greater level, however visually, small percentages of IMF can be determined in samples (FIG. 12) largely consisting of TUN at the 5% or greater level from intensity of peak at d-spacing of ˜9.46 A, while at higher levels, other peaks can be followed such as the increase in peak at d-spacing of ˜11.4 A amongst others. In FIG. 12, spectrum 1 is 1% IMF, 99% TUN; spectrum 2 is ˜3% IMF, 97% TUN; spectrum 3 is ˜5% IMF, 95% TUN; and spectrum 4 is ˜10% IMF, 90% TUN.

Rietveld analysis was able to quantify the level of TUN in the UZM-39 coherently grown composite structure at the 10% or greater level, however FIG. 13 shows that, visually, small percentages of TUN can be seen in samples largely consisting of IMF at the 5% or greater level from intensity of peak at d-spacing ˜12.25 A, while at higher levels, other peaks can be followed such as the increase in peak at d-spacing of ˜9.63 A amongst others. In FIG. 13, spectrum 1 is ˜1% TUN, 99% IMF; spectrum 2 is ˜3% TUN, 97% IMF; spectrum 3 is −5% TUN, 95% IMF; and spectrum 4 is −10% TUN, 90% IMF.

EXAMPLE 31

44.9 g of NaOH, (97%) was dissolved in 1122.3 g water. To this solution was added 10.8 g liquid sodium aluminate (22.9% Al₂O₃, 20.2% Na₂O) followed by 105.9 g Ultrasil VN3 (90% SiO₂, available from Evonik) to form a first mixture. Separately, 53.5 g 1,4-dibromobutane, (99%), was combined with 62.6 g 1-methylpyrrolidine, (97%) to form a second mixture. The second mixture was added to the first mixture to create the final reaction mixture. Last, 1 g of the layered material UZM-8 was added and the mixture was stirred vigorously for 1-2 hours before transferring to a 2 L stirred autoclave. The final reaction mixture was digested at 160° C. for 7 days while stirring at 200 rpm. The product was isolated by filtration and identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 12.40, Na/Al of 0.21, N/Al of 1.10, C/N of 7.06.

EXAMPLE 32

NaOH, Al(OH)₃, Ga(NO3)3.9H₂O, Ludox AS-40, 1,4-dibromobutane, 1-methylpyrrolidine, water and layered material UZM-8 were combined to form a mixture of composition 0.5Al2O₃:0.5 Ga₂O₃:65.4 SiO₂:24.6 Na₂O:9.9 C₄Br₂:29.4 1-MP:2636 H₂O and stirred vigorously for 1-2 hours before transferring to a 2 L stirred autoclave. The final reaction mixture was digested at 160° C. for 150 hours while stirring at 250 rpm. The product was isolated by filtration and identified as UZM-39 by XRD. Analytical results showed this material to have the following molar ratios, Si/Al of 21.61, Si/Ga of 31.35, Si/(Al+Ga) of 12.79, Na/(Al+Ga) of 0.10, N/(Al+Ga) of 0.91, C/N of 7.39.

EXAMPLE 33

A UZM-39 containing a high quantity of TUN and low quantity of IMF in the H+ form was loaded into a vertical steamer. The UZM-39 was exposed to 100% steam at 725° C. for 12 hours or 24 hours. The starting UZM-39 had a BET surface area of 385 m²/g, pore volume of 0.248 cm³/g, and micropore volume of 0.180 cm³/g. After 12 hours of steaming, the UZM-39 was still identified as UZM-39 by XRD though the intensity of the first 5 peaks had increased to strong, strong, very strong, strong and medium respectively. All other peaks were at positions and intensities described in Table B. The material had a BET surface area of 331 m²/g, pore volume of 0.243 cm³/g, and micropore volume of 0.151 cm³/g. After 24 hours of steaming, the UZM-39 was still identified as UZM-39 by XRD though the intensity of the first 5 peaks had increased to medium-strong, strong, strong, medium-strong and medium respectively. All other peaks were at positions and intensities described in Table B. The material had a BET surface area of 327 m²/g, pore volume of 0.241 cm³/g, and micropore volume of 0.150 cm³/g.

EXAMPLE 34

A UZM-39 containing a high quantity of TUN and low quantity of IMF in the H+ form was put into a round bottom flask containing 6N HNO₃ and outfitted with a condenser and stirrer. The mixture containing UZM-39 and HNO₃ was boiled at reflux for 8 or 16 h. The resulting material was filtered, washed and dried. XRD analysis showed the material to be UZM-39 consistent with Table B.

EXAMPLE 35

The product generated by the synthesis described in Example 1 was bound with Si O₂ in a 75:25 weight ratio by combining 6.71 g Ludox AS-40, 8.31 g UZM-39 and 10.79 g water. This mixture was then evaporated while stirring to form the bound UZM-39/SiO₂. The bound material was then calcined using a 2° C./minute ramp to 550° C., holding for 3 hours and then cooling to room temperature. The 20 to 60 mesh fraction was isolated and then used as the catalytic composite in a chemical reaction to form ethylbenzene and xylenes.

Benzene and propane were fed at a 2:1 mole ratio into a reactor at 410 psig along with a hydrogen stream such that the hydrogen to hydrocarbon mole ratio was about 3.5. Multiple conditions where then set starting at about 425° C. and 1.8 LHSV (Table 2 and Table 3 Column 1) and continuing to 485° C. and 1.8 LSVH (Table 2 and Table 3 Column 2); continuing again to 535° C. and 1.8 LHSV (Table 2 and Table 3 Column 3); continuing again to 535° C. and 3 LHSV (Table 2 and Table 3 Column 4); and finally continuing to 575° C. and 3 LHSV (Table 2 and Table 3 Column 5). Table 2 shows the percent of benzene and propane conversion to other compounds. Table 3 shows the toluene plus C8 aromatic yield calculated by multiplying selectivity to product with benzene conversion.

TABLE 2 Percent Conversion Column 1 Column 2 Column 3 Column 4 Column 5 Benzene  7.43 16.15 26.19 22.90 26.79 Propane 57.58 61.58 81.35 68.79 86.50

TABLE 3 Yield Column 1 Column 2 Column 3 Column 4 Column 5 Toluene plus 1.9 4.9 14.7 12.5 13.4 C8 aromatic

The experiment was repeated using bound MFI catalyst as a comparative example. The process of the invention showed about 2-3 times the selectivity to C8 aromatics as compared to the results when using the bound MFI. Furthermore, the process of the invention resulted in very little formation of cyclohexane which in turn increases the purity of a potential benzene cut.

EXAMPLE 36

UZM-39A was synthesized from a gel composition 1 Al₂O₃:65.4 SiO₂:24.6 Na₂O:9.91 1,4-dibromobutane:29.42 N-methylpyrrolidine:2636 H₂O by dissolving NaOH in water and then adding liquid sodium aluminate to the sodium hydroxide solution. Ultrasil VN3 was then added as the silica source prior to the addition of UZM-8 layered seed and then 1,4-dibromobutane and N-methylpyrrolidine to form the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 2 L stirred autoclave. The final reaction mixture was digested at 50° C. for 24 h then at 160° C. for 7 days while stirring. The product was isolated by filtration. The product was identified as UZM-39 by XRD. The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion-exchanged with 1 M ammonium nitrate solution.

UZM-39B was synthesized from a gel of composition 1 Al₂O₃:36 SiO₂:9.59 Na₂O:6.52 1,5-dibromopentane:18.95 N-methypyrrolidine:1080 H₂O by dissolving NaOH in water then adding Al(OH)₃ to the sodium hydroxide solution. Ludox AS-40 was then added as the silica source prior to the addition of UZM-8 layered seed and then 1,5-dibromobutane and N-methylpyrrolidine to form the final reaction mixture. The final reaction mixture was vigorously stirred and transferred to a 2 L stirred autoclave. The final reaction mixture was digested at 170° C. for 6 days while stirring. The product was isolated by filtration. The product was identified as a high IMF content UZM-39 by XRD. The product generated by this synthesis was calcined under flowing air at 600° for 6 hours. It was then ion-exchanged with 1 M ammonium nitrate solution.

Each of UZM-39A and UZM-39B were extruded as 1/16″ cylinders in a 75/25 zeolite/Al2O3 formulation and the extrudates dried and calcined at 550° C. for 3 hours. The extrudates were crushed and meshed to 60-180 mesh before testing. These catalyst particles were then loaded in a FCC type riser reactor and fluidized in a flow of H₂. After 0.5 hrs at 400° C. the temperature was raised to the reaction temperature of 550° C. Dried biomass of ground oak chips was then introduced in the reactor by switching the lift gas to the feed sampling manifold. Experiments were conducted at a catalyst:biomass volume ratio of 8. During the duration of the experiment, the biomass and catalyst were intimately mixed during fluidization and the condensable portion of the vapor phase products were collected in traps with toluene and isopropanol solvent. These trap solutions were analyzed by GC, as was a rinse liquid from the reactor which recovered condensed products from the reactor walls. Vapor from the reactor outlet flowed through the two traps in an ice bath. Products collected in the two traps consisted mainly of water and organic components. Both liquids were submitted for water and organic components analysis. Depending on the catalyst properties and reaction conversion, hundreds of species may be observed. However, only 32 major species have been identified. These 32 species were grouped into several groups: aromatics, non-aromatic hydrocarbons, alcohols, ketones, aldehydes, acids, phenols, esters, nitriles, and furans. Unidentified species from the GC result are grouped as “unknowns/other oxygenates”. The amount of liquid organic products were estimated based on the reference component (C₁₂ paraffin of known concentration) pre-mixed into solvent. All analytical results (coke, water, CO/CO₂ and light hydrocarbons in gas phase, and components in liquid phase) were normalized by the biomass feed in order to calculate product yields (wt %). Typically a total product yield (mass balance) of less than 100% was observed since some heavy components were not measured. For example, the heavy deposits on the reactor wall, if any, during the test were not included. The combination of these analyses provided two levels of detail regarding product information. One was the major products distribution categorized as coke, water, CO, CO₂, CH₄, C₂H₄, and total organics. Another was the yields of major liquid organic component produced including aromatics, non-aromatic hydrocarbons, alcohols, ketones, aldehydes, acids, phenols, esters, nitriles, and furans. The amounts of liquid organic products were estimated based versus a known amount of dodecane pre-mixed into solvent. The spent catalyst was analyzed for percent carbon and the gaseous products were analyzed for CO, CO₂ and light hydrocarbons with an on-line gas analyzer. Vapor from the reactor outlet flowed through the two traps held in an ice bath. Products collected in the two traps consisted mainly of water and organic components. Both liquids were submitted for water and organic components analysis. Depending on the catalyst properties and reaction conversion, hundreds of species could be observed in some cases. However, only 32 major species were identified. These 32 species were grouped into several groups: aromatics, non-aromatic hydrocarbons, alcohols, ketones, aldehydes, acids, phenols, esters, nitriles, and furans. Unidentified species from the GC result are grouped as “unknowns/other oxygenates”. The amounts of liquid organic products were estimated based on the reference component, the C₁₂ paraffin of known concentration pre-mixed into solvent. All analytical results (coke, water, CO/CO₂ and light hydrocarbons in gas phase, and components in liquid phase) are normalized by the biomass feed in order to calculate product yields (wt %). Typically a total product yield (mass balance) of less than 100% was observed since some heavy components were not measured. For example, the heavy deposits on the reactor wall, if any, during the test were not included. The combination of these analyses provided two levels of detail regarding product information. One was the major products distribution categorized as coke, water, CO, CO₂, CH₄, C₂H₄, and total organics. Another was the yields of major liquid organic component produced (aromatics, non-aromatic hydrocarbons, alcohols, ketones, aldehydes, acids, phenols, esters, nitriles, and furans). All analytical results (coke, water, CO/CO₂ and light hydrocarbons in gas phase, and components in liquid phase) were normalized by the biomass feed in order to calculate product yields (wt %).

The resulting data in Table 4 shows that UZM-39 gave a good yield of low oxygen bio-mass derived pyrolysis oil with a very high yield to aromatics and other hydrocarbons. By comparison, thermal pyrolysis using only sand gave a good yield of low oxygen bio-mass derived pyrolysis oil, but little of that product was an aromatic or other hydrocarbon. Large pore zeolites, including a FAU type (US-Y), MOR and MTW, were tested as comparative catalysts, and showed small yields of pyrolysis oil with small yields of aromatics and other hydrocarbons.

TABLE 4 75% 75% 30% 75% 75% UZM- UZM- US- MOR/ MTW/ 39A/ 39B/ sand Y/SiO2 Al2O3 Al2O3 Al2O3 Al2O3 Yield of 17 8 5 3 9 10 low oxygen biomass- derived pyrolysis oil (wt %) Yield (wt %) of: Ketones 0.90 1.20 0.14 Aldehydes 1.03 0.93 Acids 3.48 0.93 Esters 0.13 Nitriles 0.13 Aromatics 0.39 1.07 2.00 1.43 4.24 4.18 Phenols 0.26 0.27 0.14 0.13 Hydro- 0.13 0.50 0.57 0.40 1.14 carbons Other 10.69 3.47 2.50 0.71 4.24 4.68 Oxygenates 

The invention claimed is:
 1. A process for producing low oxygen biomass-derived pyrolysis oil comprising contacting a carbonaceous biomass feedstock with a microporous crystalline zeolitic catalyst at pyrolysis conditions to produce pyrolysis gases comprising hydrocarbons, the catalyst catalyzing a deoxygenation reaction converting at least a portion of the oxygenated hydrocarbons into hydrocarbons and removing the oxygen as carbon oxides and water; and condensing a condensable portion of the pyrolysis gases to produce low oxygen biomass-derived pyrolysis oil; wherein the catalyst comprises: a. a catalyst comprising a coherently grown composite of TUN and IMF zeotypes having a three-dimensional framework of at least AlO₂ and SiO₂ tetrahedral units and an empirical composition in the as synthesized and anhydrous basis expressed by an empirical formula of: Na_(n)M_(m) ^(k+)T_(t)Al_(1-x)E_(x)Si_(y)O_(z) where “n” is the mole ratio of Na to (Al+E) and has a value from approximately 0.05 to 0.5, M represents at least one metal selected from the group consisting of zinc, Group 1 (IUPAC 1), Group 2 (IUPAC 2), Group 3 (IUPAC 3), and the lanthanide series of the periodic table, and any combination thereof, “m” is the mole ratio of M to (Al+E) and has a value from 0 to 0.5, “k” is the average charge of the metal or metals M, T is the organic structure directing agent or agents derived from reactants R and Q where R is an A,Ω-dihalogen substituted alkane having from 3 to 6 carbon atoms and Q is at least one neutral monoamine having 6 or fewer carbon atoms, “t” is the mole ratio of N from the organic structure directing agent or agents to (Al+E) and has a value of from about 0.5 to about 1.5, E is an element selected from the group consisting of gallium, iron, boron and combinations thereof, “x” is the mole fraction of E and has a value from 0 to about 1.0, “y” is the mole ratio of Si to (Al+E) and varies from greater than 9 to about 25 and “z” is the mole ratio of O to (Al+E) and has a value determined by the equation: z=(n+k·m+3+4·y)/2 and is characterized in that it has TUN regions and IMF regions that are coherently aligned so that the [010]_(TUN) zone axis and the [001]_(IMF) zone axis are parallel to each other and there is continuity of crystal planes of type (002)_(TUN) and (060)_(IMF), where the indexing is referred to monoclinic C_(2/m) and orthorhombic C_(mem) unit cells for TUN and IMF respectively; wherein the catalyst is further characterized in that it has the x-ray diffraction pattern having at least the d-spacings and intensities set forth in Table A1: TABLE A1 2θ d (Å) I/Io % 7.17-7.21 12.25-12.31 vw-m  7.5-8.1* 11.78-10.91 w-m 8.88 9.95 m 9.17 9.63 w-m 12.47-12.62 7.09-7.00 w-m 17.7 5.01 vw-m 22.8-23.2 3.90-3.83 vs 23.39-23.49 3.80-3.78 m-s 25.01-25.31 3.56-3.52 m 28.74-29.25 3.10-3.05 w-m 45.08-45.29 2.01-2.00 w *composite peak consisting of multiple overlapping reflections.


2. The process of claim 1 wherein the hydrocarbons produced include aromatic compounds and the selectivity to aromatic compounds within the condensable portion of the pyrolysis gases is greater than 33% by weight.
 3. The process of claim 1 wherein the hydrocarbons produced include aromatic compounds and the selectivity to aromatic compounds within the condensable portion of the pyrolysis gases is greater 50% by weight.
 4. The process of claim 1 wherein the hydrocarbons produced include aromatic compounds and the yield of aromatic compounds is greater than 2% by weight based upon the biomass.
 5. The process of claim 1 wherein the hydrocarbons produced include aromatic compounds and the yield of aromatic compounds is greater than 3% by weight based upon biomass.
 6. The process of claim 1 wherein the pyrolysis conditions include a temperature from about 300° C. to about 800° C.
 7. The process of claim 1 wherein the catalyst is in a fluidized state.
 8. The process of claim 1 wherein the step of pyrolyzing the carbonaceous biomass feedstock comprises pyrolyzing the carbonaceous biomass feedstock in the presence of the catalyst using a catalyst-to-carbonaceous biomass feedstock ratio of about 0.1 to about
 200. 9. The process of claim 1 wherein Q is a 1:1 mixture of 1-methylpyrrolidine and dimethylethylamine.
 10. The process of claim 1 wherein R is an A,Ω-dihalogen substituted alkane having between 3 and 6 carbon atoms.
 11. The process of claim 1 where R is selected from the group consisting of 1,3-dichloropropane, 1,4-dichlorobutane, 1,5-dichloropentane, 1,6-dichlorohexane, 1,3-dibromopropane, 1,4-dibromobutane, 1,5-dibromopentane, 1,6-dibromohexane, 1,3-diiodopropane, 1,4-diiodobutane, 1,5-diiodopentane, 1,6-diiodohexane and combinations thereof.
 12. The process of claim 1 where Q is selected from the group consisting of 1-ethylpyrrolidine, 1-methylpyrrolidine, 1-ethylazetidine, 1-methylazetidine, triethylamine, diethylmethylamine, dimethylethylamine, trimethylamine, dimethylbutylamine, dimethylpropylamine, dimethylisopropylamine, methylethylpropylamine, methylethylisopropylamine, dipropylamine, diisopropylamine, cyclopentylamine, methylcyclopentylamine, hexamethyleneimine, and combinations thereof.
 13. The process of claim 1 wherein the coherently grown composite of TUN and IMF zeotypes is thermally stable up to a temperature of greater than 600° C.
 14. The process of claim 1 wherein the coherently grown composite of TUN and IMF zeotypes has a micropore volume as a percentage of total pore volume of greater than 60%. 